A Study Of Indentation Cracking In Brittle Materials Using Cohesive Zone Finite Elements, Kurt E. Johanns

Doctoral Dissertations

Cohesive zone finite element simulations of pyramidal indentation cracking in brittle materials have been carried out in order to: (1) critically examine indentation cracking models that relate fracture toughness to indentation data; (2) determine the underlying physical mechanisms of indentation crack growth from a continuum view and their relationship to material properties; (3) explore the influence of indenter geometry on crack extension; and (4) provide a platform from which future simulations can add more complex material behavior as well as guidance for experimental measurements of fracture toughness. Standard fracture toughness geometries in addition to simplified indentation geometries were simulated in …

Cracking In Cycloaliphatic Epoxy/Aluminum Composite Electrical Bushings, Keith Alan Parker

Doctoral Dissertations

The problem of cracking in electrical apparatus bushings as a result of thermal stresses was investigated. The bushings were composed of cycloaliphatic epoxy insulators with embedded aluminum conductors. The problem is due to the difference in coefficients of thermal expansion of the two materials. A solution to the problem had been to coat the conductors before they were formed together with the epoxy insulators. The coating was assumed to prevent cracking by allowing movement between the two materials as their dimensions changed during thermal expansion and contraction. The contribution of the coating was to be established.

The hypothesis was that …