Evaluating Measurement Of Strain Hardening Method For Mechanical Assessment Of Geomembrane Service Life In Msw Landfills, Alaa Alsharaballi

Theses and Dissertations

The increased household production result in more construction of municipal solid waste (MSW) landfills and lagoons. One major part of these engineering projects is high-density polyethylene (HDPE) geomembrane. Geomembrane is an impermeable layer that used along bottom and sides of landfills and lagoons to contain the leachate and to protect the groundwater. Although of their chemicals resistance and high strength, it can be aged under service conditions such as high temperature, ultraviolet (UV) light, and chemicals exposure. These conditions accelerate oxidation of geomembrane and lead to brittle behavior and stress cracking which reduce its service life.

Our objective in this …

Development Of A Supplier’S Delivery Time And Delivered Quality Performance Index And Assessment Of Alternative Decisions Regarding Underperforming Suppliers For The Aerospace Industry, Clint Saidy

Theses and Dissertations

This study investigates current practices of supplier’s delivery assessment so that a comprehensive index and a cost function model could be properly developed. Following a thorough literature review, a framework was created based on a penalty cost function that integrates both suppliers’ ability to deliver on time, as well as suppliers’ capability to deliver good quality. Afterward, suppliers could then be ranked and placed either in good standing, or transversely on probation. Underperforming suppliers face three potential outcomes based on current literature: (1) switching supplier, (2) increase collaboration, (3) maintaining the status quo. The decision vis-à-vis failing suppliers is based …

Assessment, Prevention And Remediation Of Corrosion In Weathering Steel Transmission Line Poles, Matthew Bruce Barragan

Theses and Dissertations

Electric utilities routinely use weathering steel (WS) in transmission line structures, capitalizing on corrosion resistance and associated cost savings. The formation of a protective iron-oxide patina on uncoated above-ground WS surfaces depends on the operating environment and exposure conditions. In fact, exposure to common aggressive environments, such as those found in sulfate-contaminated industrial areas and chloride-laden coastal areas, may dramatically hinder the corrosion resistance of WS transmission line structures.

To assess the corrosion behavior of WS transmission line poles, field inspections were conducted at five test sites comprising diverse operating environments and pole designs. These sites included three locations in …