Phase Formation And Thermal Conductivity Of Zirconium Carbide, Yue Zhou

Doctoral Dissertations

“This research focused on the synthesis and phase formation of zirconium carbide with different carbon contents, and lattice thermal conductivity of zirconium carbide with different carbon vacancy, hafnium, and oxygen contents.

Nominally pure phase ZrC_x was synthesized by solid-state reaction of zirconium hydride (ZrHs) and carbon black at a temperature as low as 1300°C. The powder synthesized at 1300C was carbon deficient ZrC_x . Carbon stoichiometry of the as- synthesized powders increased as the synthesis temperature increased. As the synthesis temperature increase, the oxygen content of ZrC_x decreased due to the increasing C site occupancy. Low stoichiometry …

Microstructural Evolution Of Zirconium Carbide (Zrcₓ) Ceramics Under Irradiation Conditions, Raul Florez

Doctoral Dissertations

A comprehensive understanding of the microstructural evolution of Zirconium Carbide (ZrC₂) ceramics under irradiation conditions is required for their successful implementation in advanced Gen-IV gas-cooled nuclear reactors. The research presented in this dissertation focusses on elucidating the ion and electron irradiation response of ZrC₂ ceramics. In the first part of the research, the microstructural evolution was characterized for ZrC₂ ceramics irradiated with 10 MeV Au³⁺ ions up to doses of 30 displacement per atom (dpa) at 800 ºC. Coarsening of the defective microstructure, as a function of dose, was revealed by transmission electron microscopy analysis. …