Open Access. Powered by Scholars. Published by Universities.®
- Publication Type
Articles 1 - 2 of 2
Full-Text Articles in Engineering
Synthesis, Structural, Optical And Mechanical Characterization Of Srb2O4 Nanorods, Rui Li, Lihong Bao, Xiaodong Li
Synthesis, Structural, Optical And Mechanical Characterization Of Srb2O4 Nanorods, Rui Li, Lihong Bao, Xiaodong Li
Faculty Publications
Single crystalline strontium borate (SrB2O4) nanorods were synthesized for the first time via a facile sol–gel route at low temperature. The SrB2O4 nanorods have a good crystalline nature with the growth direction along the [511] orientation and they are transparent from the ultraviolet to the visible regimes. Nanoscale three-point bending tests were performed directly on individual nanorods to probe their mechanical properties using an atomic force microscope. The elastic modulus of SrB2O4 nanorods was measured to be 158.2 ± 2.8 GPa, exhibiting a significant increase compared with other borate nanostructures …
Polydimethylsiloxane Mechanical Properties Measured By Macroscopic Compression And Nanoindentation Techniques, Zhixin Wang
Polydimethylsiloxane Mechanical Properties Measured By Macroscopic Compression And Nanoindentation Techniques, Zhixin Wang
USF Tampa Graduate Theses and Dissertations
In this thesis, the relationship between the elastic modulus of PDMS and the base/agent ratio (the amount of crosslinking) is studied. Reliable macroscopic compression test instrument was developed. Preload method was applied for the nanoindentation flat punch test to develop full contact.
In chapter 2, an easy instrument setup for macroscopic compression test is described. A series of PDMS samples with different base/agent ratios were tested using the macroscopic compression method. The relationship between PDMS elastic modulus and its base/agent ratio was established.
In chapter 3, PDMS nanoindentation DMA tests provide stable data with different test control models. The storage …