Load-Bearing Capacity Of Corroded Reinforced Concrete Structures Caused By Carbonation And Exposed To Xc4, Esko Sistonen
Load-Bearing Capacity Of Corroded Reinforced Concrete Structures Caused By Carbonation And Exposed To Xc4, Esko Sistonen
International Conference on Durability of Concrete Structures
Concrete corrosion can be visualized as a combination of chemical reaction on concrete and electrochemical reaction on steel reinforcement. Failure of steel reinforcement due to corrosion can inflict significant stress on concrete during load distribution. As such, it is necessary to analyse the long-term effects of corrosion on the load bearing capacity and bending strength of steel reinforcement. This research investigated the mechanical and electrochemical properties of concrete exposed to long-term corrosion for a period of 16 years. Non-destructive testing like crack width measurements, visual examination, electrochemical measurements using Galva Pulse and determination of average chloride content were undertaken to …
Preliminary Investigation Into The Rate Of Carbonation Of Concrete Blocks Under Normal Production Yard Conditions, Aimee Byrne, Eanna Nolan
Preliminary Investigation Into The Rate Of Carbonation Of Concrete Blocks Under Normal Production Yard Conditions, Aimee Byrne, Eanna Nolan
Conference papers
The release of CO2 from calcination during the manufacture of cement can be partially or fully offset by the CO2 it naturally absorbs during its lifetime. This paper reports results from a preliminary investigation into the rate of carbonation in concrete blocks stacked in a production yard over a period of 6 months. The blocks were stacked in a normal manner under natural exposure conditions. Carbonation progress was determined by splitting the blocks and spraying the freshly exposed surface with a phenolphthalein solution at intervals over the test period. It was found that the rate of the carbonation front progression …