Effect Of Superabsorbent Polymer On 3d Printing Characteristics As Rheology-Modified Agent, Yu Cun Gu, Kamal H. Khayat
Effect Of Superabsorbent Polymer On 3d Printing Characteristics As Rheology-Modified Agent, Yu Cun Gu, Kamal H. Khayat
Civil, Architectural and Environmental Engineering Faculty Research & Creative Works
This study aims to investigate the effects of two superabsorbent polymer (SAP) types, S1 and S2 (with continual absorption and rapid desorption, respectively) as rheology-modified agent on 3D printing characteristics. Three base mixtures were selected with different thixotropic behaviors (i.e., mixtures with high re-flocculation (τfloc), high structuration rate (Athix), and both low τfloc and Athix, respectively). The initial mini-slump flow of 190±10 mm was secured by adjusting superplasticizer (SP) or water demand (increasing w/b by either 0.025 or 0.05). An extrudable region was determined within the range of τfloc (200-890 Pa) and Athix (15-60 Pa/min). The use of the S2 …
Synergistic Effect Of Shrinkage Mitigating Materials On Rheological Properties Of Flowable And Thixotropic Cement Paste, Kamran Aghaee, Ricarda Sposito, Kamal Khayat
Synergistic Effect Of Shrinkage Mitigating Materials On Rheological Properties Of Flowable And Thixotropic Cement Paste, Kamran Aghaee, Ricarda Sposito, Kamal Khayat
Civil, Architectural and Environmental Engineering Faculty Research & Creative Works
This study investigates the effect of individual and combined additions of CaO-based expansive agent (EA), shrinkage reducing admixture (SRA), and super absorbent polymer (SAP) on key characteristics of flowable cement paste mixtures proportioned with a water-to-cement ratio of 0.40. Of special interest is the effectiveness of these admixtures to mitigate shrinkage of cementitious materials for 3D printing. Static and dynamic yield stress, plastic and apparent viscosities, and thixotropy were evaluated at 20-min intervals up to 90 min. Compressive strength development and autogenous shrinkage were also determined. A factorial design approach was developed to evaluate the synergetic effects of the shrinkage …