Effect Of Aging And Deformation On The Microstructure And Properties Of Fe-Ni-Ti Maraging Steel, A Shekhter, H I. Aaronson, M K. Miller, S P. Ringer, E V. Pereloma

Faculty of Engineering and Information Sciences - Papers: Part A

The age-hardening behavior of Fe−25.3Ni−1.7 Ti (wt pct) alloy both in undeformed specimens and in specimens cold deformed by 10 or 20 pct prior to aging was studied. The microstructural changes during aging were observed using transmission electron microscopy (TEM) and atom probe analysis and there were related to the mechanical properties as measured by microhardness and shear punch testing. An excellent combination of hardness, strength, and ductility was achieved after only 5 seconds aging at 550°C. We propose that this rapid strengthening is due to a dislocation friction effect arising from the formation of a fine dispersion of Ni−Ti …