Studies On The Inhibition Of Yki-05 Corrosion Inhibitor To 907a Steel In Different Immersed Environments, Hui Yu, Jian-Hua Wu, Hong-Ren Wang, Jian-Hua Qian, Guang-Zhang Chen
Studies On The Inhibition Of Yki-05 Corrosion Inhibitor To 907a Steel In Different Immersed Environments, Hui Yu, Jian-Hua Wu, Hong-Ren Wang, Jian-Hua Qian, Guang-Zhang Chen
Journal of Electrochemistry
The inhibition of YKI-05 Corrosion inhibitor in different conditions was studied using potentiodynamic polarization technique. The resuled shown that (i) the inhibitor film layer was formed stably on the surface of 907A steel electrode when it was persistently immersed in static seawater and the inhibition efficiency reached 90% or so. The inhibition mechanism is negative catalytic effect. (ii)the inhibitior film layer was not stable when the electrode was periodically immersed in seawater and was destroyed more significantly with the increase of electrode exposing time. The film was only a covered layer on the surface of electrode and it retarded both …
Electrochemical Techniques For Measuring Anti-Corrosion Behavior Of The Thin Corrosion Inhibitor Layer To The 907a Steel, Yong-Tao Zhao, Jian-Hua Wu, Fan-Cai Chen, Zhong-Ping Gao, Jia Wang, Chang-Jiu Zhao
Electrochemical Techniques For Measuring Anti-Corrosion Behavior Of The Thin Corrosion Inhibitor Layer To The 907a Steel, Yong-Tao Zhao, Jian-Hua Wu, Fan-Cai Chen, Zhong-Ping Gao, Jia Wang, Chang-Jiu Zhao
Journal of Electrochemistry
The corrosion inhibiting behavior of 907A steel,which was covered with thin inhibitor layers in moist seawater atmosphere,was studied.The electrochemical measurements,including EIS method and the coulostatic method,were used to atmospheric corrosioed monitor(ACM)under thin inhibitor layers to determine its corrosion rate.The results shown that the application of electrochemical methods such as the coulostatic technique and EIS could readily detect the on going process of film formation. Hence, the rapid evaluation of the thin inhibitor layers for 907A steel might be possible.
An Investigation Of Inhibition Mechanism Of Cerium For Aluminum Alloy 2024-T3, Min Hua Shao, Yan Fu, Rong Gang Hu, Chang-Jian Lin
An Investigation Of Inhibition Mechanism Of Cerium For Aluminum Alloy 2024-T3, Min Hua Shao, Yan Fu, Rong Gang Hu, Chang-Jian Lin
Journal of Electrochemistry
Cerium compounds are promising inhibitors for aluminum alloy. However, the inhibition mechanism is not very clear. Scanning microreference electrode(SMRE)technique was used to probe the potential imaging of Al 2024 T3 in NaCl and CeCl 3 solution. The results of SMRE showed that in NaCl solution a severe localized corrosion occurred on the surface of Al 2024 specimen at once and maintained for a long time. The corrosion activity of Al alloy in CeCl 3 decreased with immersion time and disappeared finally. Additionally, the competition of inhibition and aggression between Ce 3+ and Cl - on Al alloy was in situ …