Thin Film Carbon Nanofuses For Permanent Data Storage, Kevin Robert Laughlin
Thin Film Carbon Nanofuses For Permanent Data Storage, Kevin Robert Laughlin
Theses and Dissertations
We have fabricated nanofuses from thin-film, arc-evaporation carbon for use in permanent data storage. Thin film carbon fuses have fewer fabrication barriers and retain the required resistivity and structural stability to work as a data storage medium. Carbon thin films were characterized for their electrical, microstructural, and chemical bonding properties. Annealing the thin-film carbon in an argon environment at 400°C reduced the resistivity from about 4*10-2 Ω cm as deposited down to about 5*10-4 Ω cm, allowing a lower blowing voltage. Nanofuses with widths ranging from 200 nm down to 60 nm were fabricated and tested. They blow …
Photoluminescence From Gan Co-Doped With C And Si, Mykhailo Vorobiov
Photoluminescence From Gan Co-Doped With C And Si, Mykhailo Vorobiov
Theses and Dissertations
This thesis devoted to the experimental studies of yellow and blue luminescence (YL and BL relatively) bands in Gallium Nitride samples doped with C and Si. The band BLC was at first observed in the steady-state photoluminescence spectrum under high excitation intensities and discerned from BL1 and BL2 bands appearing in the same region of the spectrum. Using the time-resolved photoluminescence spectrum, we were able to determine the shape of the BLC and its position at 2.87 eV. Internal quantum efficiency of the YL band was estimated to be 90\%. The hole capture coefficient of the BLC …