Josephson-Vortex Flow Resistance In Bi2sr2ca2cu3oy Single Crystals And Its Possible Application In The Manipulation Of Spin And Charge Textures In Diluted Magnetic Semiconductors, Xiaolin Wang, C T Lin, B Liang, S Yu, S Ooi, K Hirata, S Y Ding, Dongqi Shi, S X. Dou, Zhi W. Lin, Jian G. Zhu
Josephson-Vortex Flow Resistance In Bi2sr2ca2cu3oy Single Crystals And Its Possible Application In The Manipulation Of Spin And Charge Textures In Diluted Magnetic Semiconductors, Xiaolin Wang, C T Lin, B Liang, S Yu, S Ooi, K Hirata, S Y Ding, Dongqi Shi, S X. Dou, Zhi W. Lin, Jian G. Zhu
Australian Institute for Innovative Materials - Papers
In this work, the flow of the Josephson vortices (JVs) has been studied for the highly anisotropic Bi2Sr2Ca2Cu3Oy (Bi2223) single crystals. A giant flow of JVs or giant positive magnetoresistance (MR) of over 500%-2000% was obtained in fields of 0.1-5 T and remained almost constant over a wide temperature range from 110 down to 4 K, in contrast to superconducting vortices (SVs), which only produced MR in the vicinity of Tc. The flow of the JVs is expected to be much faster than that of SVs. It is proposed …
Single-Crystal Growth And Anisotropic Magnetic Properties Of Nonstoichiometric Three-Layer Sodium Cobalt Oxides, Dapeng Chen, Xiaolin Wang, C T Lin, S X. Dou
Single-Crystal Growth And Anisotropic Magnetic Properties Of Nonstoichiometric Three-Layer Sodium Cobalt Oxides, Dapeng Chen, Xiaolin Wang, C T Lin, S X. Dou
Australian Institute for Innovative Materials - Papers
Large single crystals of α-NaxCoO2 (x=0.91, 0.92, and 0.93) have been successfully fabricated by using the traveling solvent floating zone method. Details on the crystal growth are discussed. The crystal structures were characterized using powder x-ray diffraction and Rietveld refinement. The magnetic susceptibility measurements show that the magnetic properties depend strongly on x. The compound was found to be antiferromagnetic at TN ≈ 20 K for x=0.91 and x=0.92, and paramagnetic for x=0.93. The in-plane and out-of-plane anisotropies were observed for the x=0.91 crystals. In addition, the derived anisotropic g-factor ratios (gab /gc) …