Adsorptive Features Of Polyacrylamide--Aluminosilicate Composites For Methylene Blue, Demet Baybaş, Ulvi̇ Ulusoy
Adsorptive Features Of Polyacrylamide--Aluminosilicate Composites For Methylene Blue, Demet Baybaş, Ulvi̇ Ulusoy
Turkish Journal of Chemistry
Polyacrylamide--montmorillonite (PAAm-Mt) and polyacrylamide--clinoptilolite (PAAm-Z) composites were prepared by cross-linked polymerization of acrylamide in dispersions of Mt and Z. The composites were characterized by FT-IR, SEM, XRD, CEC, and PZC analysis. The adsorptive features of PAAm-Mt and PAAm-Z for methylene blue (MB) were investigated by their relevance to initial dye concentration, temperature, contact time, PZC, and pH. The monolayer adsorption capacities were 0.14 and 0.08 mol kg$^{-1}$ for PAAm-Z and PAAm-Mt, respectively. The changes in pH of MB solution had an insignificant influence on their adsorption capacities. The values of enthalpy and entropy changes were positive ($\Delta $H$_{PAAm-Mt}$ = 7.6 …
Investigation Of Long-Term Water Absorption Behavior Of Carbon Fabric Reinforced Epoxy Composites Containing Hydrophobic Nanosilica, Nurten Eki̇n, Mehmet Gali̇p İçduygu, Ahmet Gültek
Investigation Of Long-Term Water Absorption Behavior Of Carbon Fabric Reinforced Epoxy Composites Containing Hydrophobic Nanosilica, Nurten Eki̇n, Mehmet Gali̇p İçduygu, Ahmet Gültek
Turkish Journal of Chemistry
hydrophobic filler containing epoxy matrix composites was investigated by keeping them in distilled water for 9 months. Aerosil R812 (8 nm) and Aerosil R972 (12 nm) were utilized at 3{\%} and 5{\%} w/w filler to resin ratio and the resin/filler mixture was combined with 12-ply carbon fabric to get 15 $\times $ 15 cm samples. Samples were molded under a hot press and for each sample 50 test samples obtained by cutting them with a water jet. The obtained samples were characterized by TG, FTIR, and SEM. The effect of water absorption was evaluated by measuring percentage water absorption and …
Preparation Of Fe$_{3}$O$_{4}$ @ Montmorillonite Composite As An Effective Sorbent For The Removal Of Lead And Cadmium From Wastewater Samples, Hande Tinas, Ece Çalişkan, Ni̇l Özbek, Süleyman Akman
Preparation Of Fe$_{3}$O$_{4}$ @ Montmorillonite Composite As An Effective Sorbent For The Removal Of Lead And Cadmium From Wastewater Samples, Hande Tinas, Ece Çalişkan, Ni̇l Özbek, Süleyman Akman
Turkish Journal of Chemistry
A magnetic Fe$_{3}$O$_{4}$ @ montmorillonite composite was prepared and used for the separation of lead and cadmium from aqueous solutions. For this purpose, magnetite (Fe$_{3}$O$_{4})$ was generated by co-precipitation of FeSO$_{4}$ and FeCl$_{3}$ onto montmorillonite. The effects of various experimental parameters such as pH of the solution, amount of sorbent, initial concentration of analytes, and contact time on the sorption efficiencies of lead and cadmium ions were investigated and optimized by applying a batch technique. The concentrations of analytes were determined by high resolution continuum source flame atomic absorption spectrometry. The maximum adsorption occurred at pH 2.0. The adsorption capacity …