Reduction Of Superconducting Transition Temperature And Flux Pinning In Al And C Codoped Mgb2 With Insight From First-Principles Calculations, Aihua Li, Xiaolin Wang, S X. Dou, Qiwen Yao, Zhenxiang Cheng, Saeid Soltanian, J M. Yoo, P Munroe
Reduction Of Superconducting Transition Temperature And Flux Pinning In Al And C Codoped Mgb2 With Insight From First-Principles Calculations, Aihua Li, Xiaolin Wang, S X. Dou, Qiwen Yao, Zhenxiang Cheng, Saeid Soltanian, J M. Yoo, P Munroe
Australian Institute for Innovative Materials - Papers
We report for the first time the Al and C codoping effect on the structures and superconductivity in MgB2. It was found that both the lattice parameters and the Tc decreased monotonically with increasing doping level of both Al and C. The Tc dropped to 27.5 and 7 K for x=0.2 and for x =0.4, respectively. The reduction of Tc for the codoping was found to be quicker than for individual Al doping and slower than for individual C doping at the same doping levels. First-principles calculations indicated that the observed decrease in Tc …
La And Nb Codoped Bifeo3 Multiferroic Thin Films On Lanio3/Si And Iro2/Si Substrates, Zhenxiang Cheng, Xiaolin Wang, Hideo Kimura, Kiyoshi Ozawa, S X. Dou
La And Nb Codoped Bifeo3 Multiferroic Thin Films On Lanio3/Si And Iro2/Si Substrates, Zhenxiang Cheng, Xiaolin Wang, Hideo Kimura, Kiyoshi Ozawa, S X. Dou
Australian Institute for Innovative Materials - Papers
Nb and La codoped BiFeO3 thin films were fabricated on oxide bottom electrodes, LaNiO3/Si and IrO2/Si, by pulsed laser deposition method. The doped BiFeO3 thin film capacitor on LaNiO3showed a remnant polarization of more than 75 µC/cm2 in a saturated hysteresis loop. The same La and Nb codoped BiFeO3 thin film capacitors on IrO2 showed a larger remnant polarization, while with a significant contribution from the leakage current. Furthermore, the doped BiFeO3 capacitor on the LaNiO3 bottom electrode showed worse fatigue resistance than the film on IrO …