Giant Interlayer Magnetoresistances And Strong Anisotropy In P-Type Sb2te3 Single Crystals, Zengji Yue, Xiaolin Wang, S X. Dou
Giant Interlayer Magnetoresistances And Strong Anisotropy In P-Type Sb2te3 Single Crystals, Zengji Yue, Xiaolin Wang, S X. Dou
Shi Xue Dou
Anisotropic interlayer magneto-transport properties have been studied over a broad range of temperatures and magnetic fields in p-type Sb2Te3 single crystals. Giant interlayer magnetoresistance (MR) of up to 400% was observed, which exhibits quadratic field dependences in low fields and becomes linear at high fields without any trend towards saturation. The interlayer MR displays strong anisotropy and is attributable to the anisotropy of the Fermi surface. The observed giant anisotropic interlayer MR could find applications in p-type Sb2Te3 based magneto-electronic devices.
The Flux Pinning Mechanism, And Electrical And Magnetic Anisotropy In Fe1.04te0.6se0.4 Superconducting Single Crystal, Mahboobeh Shahbazi-Manshadi, Xiaolin Wang, S X. Dou, H Fang, C T. Lin
The Flux Pinning Mechanism, And Electrical And Magnetic Anisotropy In Fe1.04te0.6se0.4 Superconducting Single Crystal, Mahboobeh Shahbazi-Manshadi, Xiaolin Wang, S X. Dou, H Fang, C T. Lin
Shi Xue Dou
The temperature and magnetic field dependences of the magnetization and critical current density of Fe1.04Te0.6Se0.4 single crystals have been investigated, and the flux pinning mechanism has been analysed. The normalized pinning force (fp Fp/F p,max) vs. h(H/Hirr) curves, are scaled using the Dew-Hughes theory, f(h) ≈ hp(1 - h)q with p 1.35 and q 3.06. The angular dependence of the resistivity under different magnetic fields shows a dip-like structure, below the superconducting transition temperature. The anisotropic value of 2 was obtained using Ginzburg-Landau theory.
Anisotropy Of Crystal Growth Mechanisms, Dielectricity, And Magnetism Of Multiferroic Bi2femno6 Thin Films, P Liu, Z X. Cheng, Y Du, L Y. Feng, H Fang, Xiaolin Wang, S X. Dou
Anisotropy Of Crystal Growth Mechanisms, Dielectricity, And Magnetism Of Multiferroic Bi2femno6 Thin Films, P Liu, Z X. Cheng, Y Du, L Y. Feng, H Fang, Xiaolin Wang, S X. Dou
Shi Xue Dou
Epitaxial Bi2FeMnO6 (BFMO) thin films deposited on various Nb:SrTiO3 substrates show that the lattice parameters are very sensitive to epitaxial strains. Compressive and tensile strains are induced to the in-plane lattice constants of the (100) and (111) oriented films, respectively, while that of the (110) oriented thin film stay unstrained. The thin films also exhibit a strongly anisotropic growth habit depending on the substrate. Spiral growth, such as in the (100) BFMO film, is unique in samples prepared by pulsed laser deposition. Extrinsic dielectric constants at low frequencies are attributed to oxygen vacancies via the Maxwell-Wagner effect. All the samples …