Synthesis And Characterization Of Dendrimer Templated Supported Bimetallic Pt-Au Nanoparticles, Huifang Lang, S. Maldonado, K. J. Stevenson, Bert D. Chandler
Synthesis And Characterization Of Dendrimer Templated Supported Bimetallic Pt-Au Nanoparticles, Huifang Lang, S. Maldonado, K. J. Stevenson, Bert D. Chandler
Chemistry Faculty Research
Bimetallic dendrimer-stabilized nanoparticles (DSNs) were used to prepare supported Pt-Au catalysts within the bulk miscibility gap for this binary system. Hydroxy-terminated generation 5 PAMAM dendrimers were used to prepare Cu0 nanoparticles (NPs). The Cu0 NPs were subsequently used to reduce K2PtCl4 and HAuCl4, preparing stabilized bimetallic Pt-Au NPs with a 1:1 stoichiometry. The stabilized NPs were adsorbed onto a high surface area silica support and thermally activated to remove the dendrimers. Transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), and infrared spectroscopy of adsorbed CO showed that this preparation route resulted in NPs in …
Characterization And Magnetic Properties Of Core/Shell Structured Fe/Au Nanoparticles, Sung-Jin Cho, Susan M. Kauzlarich, Justin Olamit, Kai Liu, Fernande Grandjean, Leïla Rebbouh, Gary J. Long
Characterization And Magnetic Properties Of Core/Shell Structured Fe/Au Nanoparticles, Sung-Jin Cho, Susan M. Kauzlarich, Justin Olamit, Kai Liu, Fernande Grandjean, Leïla Rebbouh, Gary J. Long
Chemistry Faculty Research & Creative Works
Au-coated Fe nanoparticles have been prepared by using a reverse micelle method through reduction of an aqueous solution. Characterizations have been carried out over time to probe the oxidation of Fe. Immediately after synthesis, the samples exhibit metallic conduction and a negative magnetoresistance, consistent with the presence of α-Fe. The temperature dependence of magnetization displays a maximum at a blocking temperature of around 150 K. After a period of 1 month, the samples exhibit insulating behavior, indicating the oxidation of the Fe core. Mössbauer spectroscopy indicates the presence of an α-Fe component and a broad distribution of local environments.