Corrosion Map For Metal Pipes In Coastal Louisiana, Sanjay Tewari

Civil, Architectural and Environmental Engineering Faculty Research & Creative Works

Transportation agencies often allow metal pipes as an option for cross drains under/along roads and highways. Metal culverts can corrode over time at various rates based on their environmental conditions (e.g., corrosive nature of coastal soils, high water table, and saltwater intrusion).

This project was focused on applying available soil data, such as spatial distribution of soil types and soil characteristics (e.g., pH and conductivity), towards creating a Geographic Information System (GIS) based map to identify corrosion zones in coastal Louisiana. The effect of the soil characteristics (pH and conductivity) was incorporated in to the published corrosion models for calculating …

Nano-Channels Early Formation Investigation On Stainless Steel 316ti After Immersion In Molten Pb-Bi, Abu Khalid Rivai, Mardiyanto Mardiyanto, Annette Heinzel

Makara Journal of Technology

Development of fuel cladding and structural materials in Pb-Bi environment, especially at high temperature, is a critical issue for the deployment of LFR (Lead alloy-cooled Fast Reactor) and ADS (Accelerator Driven Transmutation System). This is because of the corrosive characteristic of Pb-Bi to metals as constituent materials of fuel cladding and structural of the reactors. Corrosion test of a high-chromium austenitic stainless steel i.e. SS316Ti in molten Pb-Bi at 550 ºC has been carried out for about 300 hours continuously. The characterization using SEM-EDS (Scanning Electron Microscopy - Energy Dispersive X-ray Spectroscopy) showed that an iron oxide as the outer …

Mechanism Of Cathodic Prevention Of Carbon Steel In Concrete, Krittin Rattakham

USF Tampa Graduate Theses and Dissertations

In this work, I aim to clarify the mechanism that allows steel to attain higher chloride threshold as it is cathodically polarized. Specifically, I seek to provide empirical information on whether an intrinsic (predominantly interfacial effects of polarization) or an extrinsic (predominantly concentration changes due to polarization) mechanism may be dominant in the beneficial effect of polarization. I carried out this experiment with 12 identical concrete specimens, each with a cast-in steel plate, constantly exposed them to high-chloride environment. The specimens were divided into 4 triplicates and polarized at 4 different level from OCP, -200, -300 to -400 mV_{SCE …}

Corrosion Degradation Mechanism Of Cbpc Coating System For Highway Bridge Steel Components, Md Ahsan Sabbir

FIU Electronic Theses and Dissertations

Coatings are widely used to mitigate corrosion of structural steel in aggressive humid environments. However, the service life is often diminished in aggressive environments. Repair of coatings can be costly due to materials, labor and environmental controls. So, in search for novel coatings, Chemically Bonded Phosphate Ceramic (CBPC) coating was investigated for marine bridge application. The research on CBPC coating considered various exposure environments such as inland, beach, salt-fog, wet and alternate wet and dry exposure to identify the degradation mechanism. To assess the corrosion damage, the coating was evaluated by visual inspection, thickness, adhesion, microscopy and X-ray diffraction.

The …

Electrochemical Methods To Characterize Drilled Shaft Deficiencies, Sarah Jo Mobley

USF Tampa Graduate Theses and Dissertations

In recent years drilled shafts have become the preferred foundation method for marine bridges. Typically, the drilled shaft is selected over traditional driven piles due to soil strata encountered, construction economy, increased lateral stiffness requirements, and/or vibration control considerations. The most critical component in drilled shaft construction is borehole stabilization. Wall sloughing or groundwater inclusion can have devastating effects on the strength of the finished shaft however recent research has shown that the materials, more specifically the slurry, used to accomplish stabilization may be having a negative impact on the durability of the finished product. This thesis investigates the durability …