Study On Mechanical Properties Of A356 Alloys Enhanced With Preformed Thixotropic Structure, Shueiwan H. Juang, Shyh-Ming Wu
Study On Mechanical Properties Of A356 Alloys Enhanced With Preformed Thixotropic Structure, Shueiwan H. Juang, Shyh-Ming Wu
Journal of Marine Science and Technology
A preformed A356 alloys with thixotropic structure (designated SSM-A356) was systematically studied on mechanical properties in order to establish the database for further investigations in forming and heat treatment. Because of the specific microstructure and characteristics, the heat treatment conditions of SSM-A356 were explored through the observations of microstructure and the measurement of micro-hardness. In the investigation of heat treatment, it was observed that the eutectic silicon was refined and spheroidized which is unlikely for conventional processing. The mechanical testing results showed that the yield and ultimate tensile strength of SSM-A356 were respectively around 115% and 34% greater than those …
Freeform Fabrication Of Zirconium Diboride Parts Using Selective Laser Sintering, Ming-Chuan Leu, Erik B. Adamek, Tieshu Huang, Greg Hilmas, Fatih Dogan
Freeform Fabrication Of Zirconium Diboride Parts Using Selective Laser Sintering, Ming-Chuan Leu, Erik B. Adamek, Tieshu Huang, Greg Hilmas, Fatih Dogan
Mechanical and Aerospace Engineering Faculty Research & Creative Works
Using the Selective Laser Sintering (SLS) process, both flexural test bars and 3D fuel injector components have been fabricated with zirconium diboride (ZrB2) powder. Stearic acid was selected as the binder. Values of SLS process parameters were chosen such that the green parts could be built with sharp geometrical features and that the sintered parts could have good mechanical properties. After binder burnout and sintering, the SLS fabricated ZrB2 test bars achieved 80% theoretical density, and the average flexural strength of the sintered samples was 195 MPa. These values demonstrate the feasibility of the SLS process for …
Properties Of Distillers Grains Composites: A Preliminary Investigation, Vanessa Cheesbrough, Kurt A. Rosentrater, Jerry Visser
Properties Of Distillers Grains Composites: A Preliminary Investigation, Vanessa Cheesbrough, Kurt A. Rosentrater, Jerry Visser
Kurt A. Rosentrater
Interest in renewable biofuel sources has intensified in recent years, leading to greatly increased production of ethanol and its primary coproduct, Distillers Dried Grain with Solubles (DDGS). Consequently, the development of new outlets for DDGS has become crucial to maintaining the economic viability of the industry. In light of these developments, this preliminary study aimed to determine the suitability of DDGS for use as a biofiller in low-cost composites that could be produced by rapid prototyping applications. The effects of DDGS content, particle size, curing temperature, and compression on resulting properties, such as flexural strength, modulus of elasticity, water activity, …