Additive manufacturing has spread widely over the past decade, especially with the availability of home 3D printers. In the future, many items may be manufactured at home, which raises two ethical issues. First, there are questions of safety. Our current safety regulations depend on centralized manufacturing assumptions they will be difficult to enforce on this new model of manufacturing. Using current US law as an example, I argue that consumers are not capable of fully assessing all relevant risks and thus continue to require protection any regulation will likely apply to plans, however, not physical objects. Second, there are intellectual …
Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming-Chuan Leu, Greg Hilmas
Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming-Chuan Leu, Greg Hilmas
Mechanical and Aerospace Engineering Faculty Research & Creative Works
An extrusion-based additive manufacturing process, called the Ceramic On-Demand Extrusion (CODE) process, for producing three-dimensional ceramic components with near theoretical density is introduced in this paper. In this process, an aqueous paste of ceramic particles with a very low binder content (< 1 vol%) is extruded through a moving nozzle at room temperature. After a layer is deposited, it is surrounded by oil (to a level just below the top surface of most recent layer) to preclude non-uniform evaporation from the sides. Infrared radiation is then used to partially, and uniformly, dry the just-deposited layer so that the yield stress of the paste increases and the part maintains its shape. The same procedure is repeated for every layer until part fabrication is completed. Several sample parts for various applications were produced using this process and their properties were obtained. The results indicate that the proposed method enables fabrication of large, dense ceramic parts with complex geometries.
A Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming-Chuan Leu, Greg Hilmas
A Novel Extrusion-Based Additive Manufacturing Process For Ceramic Parts, Amir Ghazanfari, Wenbin Li, Ming-Chuan Leu, Greg Hilmas
Mechanical and Aerospace Engineering Faculty Research & Creative Works
An extrusion-based additive manufacturing process, called the Ceramic On-Demand Extrusion (CODE) process, for producing three-dimensional ceramic components with near theoretical density is introduced in this paper. In this process, an aqueous paste of ceramic particles with a very low binder content ( < 1 vol%) is extruded through a moving nozzle at room temperature. After a layer is deposited, it is surrounded by oil (to a level just below the top surface of most recent layer) to preclude non-uniform evaporation from the sides. Infrared radiation is then used to partially, and uniformly, dry the just-deposited layer so that the yield stress of the paste increases and the part maintains its shape. The same procedure is repeated for every layer until part fabrication is completed. Several sample parts for various applications were produced using this process and their properties were obtained. The results indicate that the proposed method enables fabrication of large, dense ceramic parts with complex geometries.