Mechanism Underlying Effect Of Expansive Agent And Shrinkage Reducing Admixture On Mechanical Properties And Fiber-Matrix Bonding Of Fiber-Reinforced Mortar, Kamran Aghaee, Taihao Han, Aditya Kumar, Kamal Khayat
Mechanism Underlying Effect Of Expansive Agent And Shrinkage Reducing Admixture On Mechanical Properties And Fiber-Matrix Bonding Of Fiber-Reinforced Mortar, Kamran Aghaee, Taihao Han, Aditya Kumar, Kamal Khayat
Materials Science and Engineering Faculty Research & Creative Works
Expansive agent (EA) and shrinkage reducing admixture (SRA) are utilized to reduce shrinkage and risk of cracking in concrete. EA compensates shrinkage by initial expansion, and SRA reduces surface tension in the pore fluid. Although EA and SRA effectively reduce shrinkage, they can impair micro-structure of concrete at high contents. The shrinkage reduction effect of EA and SRA is well known; however, there is limited knowledge about their negative effect on microstructure and fiber matrix interfacial transition zone (ITZ). The current study explores the effect of using 10 % CaO-based EA, 2 % SRA, and their combination on mechanical, shrinkage, …
Investigation Of Deformation Behavior Of Additively Manufactured Aisi 316l Stainless Steel With In Situ Micro-Compression Testing, Fei Teng, Ching-Heng Shiau, Cheng Sun, Robert C. O'Brien, Michael D. Mcmurtrey
Investigation Of Deformation Behavior Of Additively Manufactured Aisi 316l Stainless Steel With In Situ Micro-Compression Testing, Fei Teng, Ching-Heng Shiau, Cheng Sun, Robert C. O'Brien, Michael D. Mcmurtrey
Materials Science and Engineering Faculty Publications and Presentations
Additive manufacturing techniques are being used more and more to perform the precise fabrication of engineering components with complex geometries. The heterogeneity of additively manufactured microstructures deteriorates the mechanical integrity of products. In this paper, we printed AISI 316L stainless steel using the additive manufacturing technique of laser metal deposition. Both single-phase and dual-phase substructures were formed in the grain interiors. Electron backscatter diffraction and energy-dispersive X-ray spectroscopy indicate that Si, Mo, S, Cr were enriched, while Fe was depleted along the substructure boundaries. In situ micro-compression testing was performed at room temperature along the [001] orientation. The dual-phase substructures …
A High-Strength Precipitation Hardened Cobalt-Free High-Entropy Alloy, Matthew Luebbe, Jiaqi Duan, Fan Zhang, Jonathan Poplawsky, Hans Pommeranke, Maalavan Arivu, Andrew Hoffman, Mario F. Buchely, Haiming Wen
A High-Strength Precipitation Hardened Cobalt-Free High-Entropy Alloy, Matthew Luebbe, Jiaqi Duan, Fan Zhang, Jonathan Poplawsky, Hans Pommeranke, Maalavan Arivu, Andrew Hoffman, Mario F. Buchely, Haiming Wen
Materials Science and Engineering Faculty Research & Creative Works
Recent Studies on Precipitation-Hardened High-Entropy Alloys (HEAs) Demonstrate their High Strength and Thermal Stability, Making Them Promising Materials for High-Temperature Structural Applications Such as Nuclear Reactors. However, Many Existing HEAs Contain Cobalt (Co), Which is Unsuitable for Nuclear Applications Because of the Long-Term Activation Issue of Co. Co is Also Expensive and Considered a Critical Material for Other Applications. Therefore, It is Desired to Exclude Co from the Composition. a Co-Free (Fe0.3Ni0.3Mn0.3Cr0.1)88Ti4Al8 HEA Was Developed and Studied in This Work. in Contrast to Previous Co-Free HEAs, This Alloy is …
Synthesizing Ti–Ni Alloy Composite Coating On Ti–6al–4v Surface From Laser Surface Modification, Yitao Chen, Joseph William Newkirk, Frank W. Liou
Synthesizing Ti–Ni Alloy Composite Coating On Ti–6al–4v Surface From Laser Surface Modification, Yitao Chen, Joseph William Newkirk, Frank W. Liou
Materials Science and Engineering Faculty Research & Creative Works
In This Work, a Ni-Alloy Deloro-22 Was Laser-Deposited on a Ti–6Al–4V Bar Substrate with Multiple Sets of Laser Processing Parameters. the Purpose Was to Apply Laser Surface Modification to Synthesize Different Combinations of Ductile TiNi and Hard Ti2Ni Intermetallic Phases on the Surface of Ti–6Al–4V in Order to Obtain Adjustable Surface Properties. Scanning Electron Microscopy, Energy Dispersion Spectroscopy, and X-Ray Diffraction Were Applied to Reveal the Deposited Surface Microstructure and Phase. the Effect of Processing Parameters on the Resultant Compositions of TiNi and Ti2Ni Was Discussed. the Hardness of the Deposition Was Evaluated, and Comparisons with …
Boro/Carbothermal Reduction Co-Synthesis Of Dual-Phase High-Entropy Boride-Carbide Ceramics, Lun Feng, William Fahrenholtz, Gregory E. Hilmas, Stefano Curtarolo
Boro/Carbothermal Reduction Co-Synthesis Of Dual-Phase High-Entropy Boride-Carbide Ceramics, Lun Feng, William Fahrenholtz, Gregory E. Hilmas, Stefano Curtarolo
Materials Science and Engineering Faculty Research & Creative Works
Dense, dual-phase (Cr,Hf,Nb,Ta,Ti,Zr)B2-(Cr,Hf,Nb,Ta,Ti,Zr)C ceramics were synthesized by boro/carbothermal reduction of oxides and densified by spark plasma sintering. The high-entropy carbide content was about 14.5 wt%. Grain growth was suppressed by the pinning effect of the two-phase ceramic, which resulted in average grain sizes of 2.7 ± 1.3 µm for the high-entropy boride phase and 1.6 ± 0.7 µm for the high-entropy carbide phase. Vickers hardness values increased from 25.2 ± 1.1 GPa for an indentation load of 9.81 N to 38.9 ± 2.5 GPa for an indentation load of 0.49 N due to the indentation size effect. Boro/carbothermal …