Electrochemical Characterization Of Positive Electrode Material Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 In Different Electrolytes, Jing-Jing Liu, Wei-Hua Qiu, Ling-Yan Yu, Hai-Lei Zhao, Tao Li
Electrochemical Characterization Of Positive Electrode Material Lini_(1/3)Co_(1/3)Mn_(1/3)O_2 In Different Electrolytes, Jing-Jing Liu, Wei-Hua Qiu, Ling-Yan Yu, Hai-Lei Zhao, Tao Li
Journal of Electrochemistry
Cathode materials LiNi_(1/3)Co_(1/3)Mn_(1/3)O_(2) were prepared by low-heating solid-state reaction.The micro-structure and morphology of as-synthesized materials have been investigated by using XRD and SEM.The compatibilities of LiNi_(1/3)Co_(1/3)Mn_(1/3)O_(2) with purchased LiPF_(6)/ EC+DMC+DEC electrolyte and prepared LiBOB/EC+DEC+EMC electrolyte have also been studied.The Li/LiNi_(1/3)Co_(1/3)Mn_(1/3)O_(2) batteries showed excellent electrochemical properties in the LiPF_(6)/ EC+DMC+DEC electrolyte.Reversible discharge capacities of 167、163、163、157、147mAh/g at 0.5C、1C、1.5C、2C、3C rate between 2.7~4.35 V,with stable cycling performances have been obtained.Comparatively,the specific capacity of 160 mAh/g at 0.5C was obtained in LiBOB/EC+DEC+DEC electrolyte,which was just a little lower than that in the other electrolyte.However,the high rate capability of the materials in LiBOB/EC+DEC+DEC was not as …
The Property Study Of Libob-Pc/Dec Electrolyte, Ying-Kun Ning, Bi-Tao Yu, Fu-Shen Li, Wei-Hua Qiu
The Property Study Of Libob-Pc/Dec Electrolyte, Ying-Kun Ning, Bi-Tao Yu, Fu-Shen Li, Wei-Hua Qiu
Journal of Electrochemistry
The new electrolyte salt LiBOB for Li-ion battery was synthesized in laboratory,and series of electrolytes of LiBOB and PC/DEC was compounded.The conductivity of the electrolytes was compared by changing the temperature and concentration.The cycling performance of charging-discharging was also compared by the charging-discharging test,the results showed that the varying regularity of conductivities and cycling stability and capacity were not always identical,but there were a suitable electrolyte for Li/ARG cell.The A.C.impedance and CV were used to test the compatibility of the most suitable electrolyte and ARG anode.Conclusion can be drawn that the ARG anode can be protected very well by SEI …