Thermodynamic Considerations Of The Corrosion Of Nickel Ferrite Refractory By Na3alf6-Alf3-Caf2-Al 2o3 Bath, Raymond Longbottom, Sharon Nightingale, Brian Monaghan

Brian Monaghan

Thermodynamic analysis was carried out to interpret the results of corrosion testing of nickel ferrite samples in cryolite-based baths. The equilibrium between cryolite-based baths and nickel ferrite was considered. Isopleths between cryolite-based baths and nickel ferrite confirmed that for the temperature range of interest (1223-1273 K) there was limited solubility of nickel ferrite in the bath. To better understand the formation of the metal from nickel ferrite, the effect of reducing potentials on nickel ferrite and nickel ferrite-cryolite-based bath systems were considered. The formation of a metal phase was predicted at relatively high pO2. The metal phase was nickel-rich at …