Influence Of Nb On The Β → Α″ Martensitic Phase Transformation And Properties Of The Newly Designed Ti-Fe-Nb Alloys, Shima Ehtemam-Haghighi, Yujing Liu, Guanghui Cao, Lai-Chang Zhang
Influence Of Nb On The Β → Α″ Martensitic Phase Transformation And Properties Of The Newly Designed Ti-Fe-Nb Alloys, Shima Ehtemam-Haghighi, Yujing Liu, Guanghui Cao, Lai-Chang Zhang
Research outputs 2014 to 2021
A series of Ti-7Fe-xNb (x = 0, 1, 4, 6, 9, 11 wt.%) alloys was designed and cast to investigate the β → α″ martensitic phase transformation, β phase stability, the resulting microstructure and mechanical properties. Phase analysis revealed that only Ti-7Fe-11Nb alloy shows a single body-centred cubic β phase microstructure while the others are comprised of β and orthorhombic α″ phases. Moreover, Nb addition up to 11 wt.% enhances the stability and volume fraction of β phase in the microstructure, hence reducing the propensity of the alloy system to form α″ phase during quenching. Compressive yield strength and hardness …
Processing Of Al-12si-Tnm Composites By Selective Laser Melting And Evaluation Of Compressive And Wear Properties, Konda Prashanth, Sergio Scudino, Anil Chaubey, Lukas Löber, Pei Wang, Hooyar Attar, Frank Schimansky, Florian Pyczak, Jürgen Eckert
Processing Of Al-12si-Tnm Composites By Selective Laser Melting And Evaluation Of Compressive And Wear Properties, Konda Prashanth, Sergio Scudino, Anil Chaubey, Lukas Löber, Pei Wang, Hooyar Attar, Frank Schimansky, Florian Pyczak, Jürgen Eckert
Research outputs 2014 to 2021
Al-12Si (80 vol%)-Ti52.4Al42.2Nb4.4Mo0.9B0.06 (at.%) (TNM) composites were successfully produced by the selective laser melting (SLM). Detailed structural and microstructural analysis shows the formation of the Al6MoTi intermetallic phase due to the reaction of the TNM reinforcement with the Al-12Si matrix during SLM. Compression tests reveal that the composites exhibit significantly improved properties (∼140 and ∼160 MPa higher yield and ultimate compressive strengths, respectively) compared with the Al-12Si matrix. However, the samples break at ∼6% total strain under compression, thus showing a reduced plasticity of the composites. Sliding wear tests were carried out for both the Al-12Si matrix and the Al-12Si-TNM …
The Heat Treatment Analysis Of E110 Case Hardening Steel, Majid Tolouei Rad, Eric Lichter
The Heat Treatment Analysis Of E110 Case Hardening Steel, Majid Tolouei Rad, Eric Lichter
Research outputs 2014 to 2021
This paper investigates mechanical and microstructural behaviour of E110 case hardening steel when subjected to different heat treatment processes includingquenching, normalizing and tempering. After heat treatment samples were subjected to mechanical and metallographic analysisand the properties obtained from applying different processes were analysed. The heat treatment process had certain effects on the resultant properties andmicrostructures obtained for E110 steel which are described in details. Quenching produced a martensitic microstructure characterized by significant increase in material’s hardness and a significant decreased in its impact energy. Annealed specimens produced a coarse pearlitic microstructure with minimal variation in hardness and impact energy. For …