Engineering Commons^™

The Angiogenic Potential Of Ph-Neutral Borophosphate Bioactive Glasses, Bradley A. Bromet, Nathaniel P. Blackwell, Nada Abokefa, Parker Freudenberger, Rebekah L. Blatt, Richard K. Brow, Julie A. Semon

Materials Science and Engineering Faculty Research & Creative Works

Borate bioactive glasses have gained attention in recent years due to their therapeutic and regenerative effects in vivo. However, borate bioactive glasses release alkaline ions, increasing the local pH and creating a toxic environment for cell culture studies. A partial compositional substitution of phosphate for borate can create a pH-neutral glass that does not significantly affect the local pH while still releasing therapeutic ions. In the present study, a series of Na-Ca-borophosphate bioactive glasses with different borate-to-phosphate ratios was evaluated in vitro and in vivo for cytotoxicity and angiogenic effects. Compared to more basic borate glasses, the pH-neutral glasses supported …

Biomaterials For Bone Regeneration, Youqu Shen

Doctoral Dissertations

"The purpose of this Ph.D. research is to investigate and improve two classes of hydroxyapatite (HA)-based biomaterials for bone repair: calcium phosphate microspheres and bioactive silicate glass scaffolds. These biomaterials were prepared with modified compositions and microstructures and then were evaluated for bone regeneration.

The open HA microspheres with dense convex surfaces and rough and porous concave surfaces were obtained by sectioning closed hollow HA microspheres. Bone regeneration with the open HA microspheres was greater than with the closed HA microsphere at 12 weeks. Hollow biphasic calcium phosphate (BCP) microspheres have been prepared with different fractions of HA and β-TCP …

3d Bioprinting Of Stem Cells And Polymer/Bioactive Glass Composite Scaffolds For Bone Tissue Engineering, Caroline Murphy, Krishna Kolan, Wenbin Li, Julie A. Semon, D. E. Day, Ming-Chuan Leu

Biological Sciences Faculty Research & Creative Works

A major limitation of using synthetic scaffolds in tissue engineering applications is insufficient angiogenesis in scaffold interior. Bioactive borate glasses have been shown to promote angiogenesis. There is a need to investigate the biofabrication of polymer composites by incorporating borate glass to increase the angiogenic capacity of the fabri-cated scaffolds. In this study, we investigated the bioprinting of human adipose stem cells (ASCs) with a polycaprolac-tone (PCL)/bioactive borate glass composite. Borate glass at the concentration of 10 to 50 weight %, was added to a mixture of PCL and organic solvent to make an extrudable paste. ASCs suspended in Matrigel …

Water-Soluble Glass Substrate As A Platform For Biodegradable Solid-State Devices, Shihab Md Adnan, Kwangman Lee, Mohammad Tayeb Ahmad Ghasr, Matthew O'Keefe, D. E. Day, Chang-Soo Kim

Materials Science and Engineering Faculty Research & Creative Works

A biodegradable glass material is utilized as a novel functional element of solid-state devices. A water-soluble borate glass substrate serves as the structural platform on which thin film device is built. The glass substrate completely dissolves in a saline solution in approximately 40 h. Intentional failure of the spiral device (RLC resonator circuit) as a result of rapid structural disintegration by dissolution is demonstrated in DC, AC, and RF ranges that agrees well with simulation. Adopting water-soluble glass elements is expected to be a viable approach to develop reliable all-inorganic biodegradable devices that are fully functional during an intended operational …

Bioactivity/Cytotoxicity Of Micro-/Nano-Materials And Novel Development Of Fiber-Optic Probes For Single Cell Monitoring, Qingbo Yang

Doctoral Dissertations

"Manufactured nano-/micro-materials (MNMs) have been widely used and their interactions with niche biological environment are highly concerned for both of their biohazardous and bioactive effects, whereas no available comprehensive evaluations or regulations have been provided yet. This dissertation thus focuses on three major aspects: 1) fundamental toxicity understandings of a typical MNMs (zinc oxide nanoparticles), 2) bioactivity evaluations of representative bioactive MNMs, and 3) development of novel micro-probes for high spatial resolution monitoring. Firstly, the NP's concentration, irradiation, hydrodynamic size, and the localized pH, ionic strength, NP zeta-potential as well as dissolved oxygen levels were found correlated with the production …

Selective Laser Sintering Of Bioactive Glass Scaffolds And Their Biological Assessment For Bone Repair, Krishna C. R. Kolan

Doctoral Dissertations

"Bone scaffold fabrication using powder-bed based additive manufacturing techniques, like the selective laser sintering (SLS) process, provides control over pore interconnectivity, pore geometry, and the overall shape of the scaffold, which aids in repairing different regions of the bone. The main objectives of this dissertation were to develop bioactive glass (BG) scaffolds using the SLS process and evaluate the scaffolds for their effectiveness in bone repair both in vitro and in vivo. 13-93 glass, a silicate based BG, and 13-93B3 glass, a borate based BG, are designed to accelerate the body's natural ability to heal itself and are used …

Inorganic Biodegradable Devices For Temporary Implants, Kassan Unda

Masters Theses

"Implantable electronic devices have great potential to benefit many health care technologies. They comprise of two different categories. The first is permanent prosthetic devices like cardiac pacemakers or nerve stimulants. The other category includes temporary devices for interventional medical monitoring and control scenarios, which lose functionality and become unnecessary after their intended operational lifetime. This can cause serious electromagnetic and biomechanical safety concerns if not removed from the body by an additional surgical operation.

This thesis focuses on exploring the feasibility of implantable inorganic bioresorbable thin film resistive devices utilizing bioactive glass as the core structural material. This device will …

Effect Of Architecture And Porosity On Mechanical Properties Of Borate Glass Scaffolds Made By Selective Laser Sintering, Krishna C. R. Kolan, Ming-Chuan Leu, Greg Hilmas, Taylor Comte

Mechanical and Aerospace Engineering Faculty Research & Creative Works

The porosity and architecture of bone scaffolds, intended for use in bone repair or replacement, are two of the most important parameters in the field of bone tissue engineering. The two parameters not only affect the mechanical properties of the scaffolds but also aid in determining the amount of bone regeneration after implantation. Scaffolds with five different architectures and four porosity levels were fabricated using borate bioactive glass (13-93B3) using the selective laser sintering (SLS) process. The pore size of the scaffolds varied from 400 to 1300 μm. The compressive strength of the scaffolds varied from 1.7 to 15.5 MPa …

Effect Of Particle Size, Binder Content And Heat Treatment On Mechanical Properties Of 13-93 Bioactive Glass Scaffolds, Krishna C. R. Kolan, Ming-Chuan Leu, Greg Hilmas, Mariano Garcia Velez

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Particle size, binder content and the post-processing schedule are important parameters that affect the microstructure, and, hence, the mechanical properties of parts produced using the indirect selective laser sintering process. 13-93 bioactive glass, with mean particle sizes ranging from 10 μm to 44 μm, is mixed with different amounts of stearic acid binder to fabricate green scaffolds. Through the design of the post-processing schedule, the time required for postprocessing the green scaffolds is reduced from the initial 80 hrs to 12 hrs. The compressive strength varies from 41 MPa for a part with~60% porosity to 157 MPa for a part …

Freeze Extrusion Fabrication Of 13-93 Bioactive Glass Scaffolds For Bone Repair, Tieshu Huang, Nikhil D. Doiphode, M. N. Rahaman, Ming-Chuan Leu, B. Sonny Bal, D. E. Day

Materials Science and Engineering Faculty Research & Creative Works

There is an increasing demand for synthetic scaffolds with the requisite biocompatibility, internal architecture, and mechanical properties for the bone repair and regeneration. In this work, scaffolds of a silicate bioactive glass (13-93) were prepared by a freeze extrusion fabrication (FEF) method and evaluated in vitro for potential applications in bone repair and regeneration. The process parameters for FEF production of scaffolds with the requisite microstructural characteristics, as well as the mechanical and cell culture response of the scaffolds were evaluated. After binder burnout and sintering (60 min at 700°C), the scaffolds consisted of a dense glass network with interpenetrating …

Selective Laser Sintering Of 13-93 Bioactive Glass, Krishna C. R. Kolan, Ming-Chuan Leu, Greg Hilmas, Mariano Garcia Velez

Mechanical and Aerospace Engineering Faculty Research & Creative Works

Bioactive glasses are more promising than biopolymers in fabricating scaffolds for bone tissue repair because they convert to hydroxyapatite, when implanted in vivo. Both direct and indirect selective laser sintering (SLS) methods of 13-93 bioactive glass were considered in this research to study the feasibility of fabricating scaffolds for bone repair applications. Stearic acid was used as the binder in the indirect method to fabricate the scaffolds. The green scaffolds underwent binder burnout and sintering at various soaking conditions between 675⁰C and 700⁰C, achieving a maximum compressive strength of 23.6 MPa, which is higher than that of the human cancellous …