Localised Galvanic Corrosion Processes In Thermal Spray Coated/Cast Aluminium Alloy Systems, David Culliton, Tony Betts, David Kennedy

Conference Papers

Cast Aluminium Alloys, because of the propensity of aluminium to react with impurities and alloying elements, are prone to developing IM impurities during the solidification process. These IM phases can act, in some fluids, as initiation sites for localised corrosion processes, resulting in degradation phenomena, such as pitting. Whilst Thermal Spray coatings can improve the wear resistance of Cast Aluminium Alloys, their corrosion performance may be hampered by the presence of through porosity within the coating.

The present work details some preliminary studies of the localised corrosion processes occurring at the interface area between a Thermal Spray coating and a …

Gtaw ايجادشده با روش جوشکاری Tini-Tic و Tini بررسی ريزساختاری پوشش, Masoud Harooni, Morteza Shamanian, Alireza Fadaei Tehrani

Masoud Harooni

هدف از انجام اين پژوهش بهبود سختي سطحي و ريزساختار فولاد ساده کربنی از نوع 52 و مقايسه ريز ساختار اين دو با هم GTAW ايجاد شده به روش جوشکاری TiNi-TiC و TiNi پوششی از بترتيب با نسبت استوکيومتری مساوي و نسبت ۲۰ Ti-Ni-C و Ti-Ni است. بدين منظور مخلوط پودری به طور جداگانه توسط روش فعال سازی مکانيکی فعال شد و سپس بر سطح TiC درصد تقويت کننده به ضخامت ۱ ميليمتر پيش نشانده شده با استفاده از روش جوشکاری قوسی St نمونه های فولادی 52 تنگستن- گاز ذوب و با فلز پايه امتزاج يافته است. جهت بررسي نوع …