The Study Of Copper Corrosion Mechanisms Using Electrochemical Experimental Techniques., Evan Grimm

Electronic Theses and Dissertations

The purpose of this study was to discover and thoroughly explain the corrosion mechanisms of copper in saltwater, tap water and deionized water, and to apply these methods and findings when testing the corrosion mechanisms of other materials. The experimental procedure consisted of measuring the open circuit potential, electrochemical impedance spectroscopy, linear sweep voltammetry, and Tafel analysis.

The copper was found to corrode at a greater rate in saltwater, followed by tap water then deionized water, with a larger difference between saltwater and tap water than between tap water and deionized water. Each reaction was found to be both kinetically …

Increasing The Corrosion Protection Of Aisi 1008 Carbon Steel By Surface Treatment With Unmodified And Benzotriazole Modified Sol-Gel Films, Shane Thomas Kelliher

Williams Honors College, Honors Research Projects

The corrosion performance of sol-gel coated AISI 1008 carbon steel was investigated in 3.5 wt% NaCl solutions of pH 7, 9, and 12 using electrochemical measurements. A corrosion inhibitor, benzotriazole (BTA) was added to the sol-gel mixture and tested as a second, modified sol-gel coating. Sol-gel films adhered evenly to metal samples and were characterized by FTIR spectroscopy. Electrochemical Impedance Spectroscopy (EIS) showed an increase in polarization resistance from blank to sol-gel coated samples (600-18,800,000 ohms). Cyclic polarization (CPP) curves showed positive hysteresis loops for blank and unmodified sol-gel coated samples which increased at high pH following the backward potential …