Corrosion Resistance Of Silane Coatings On Aluminum And Magnesium Alloys, John Demopoulos
Corrosion Resistance Of Silane Coatings On Aluminum And Magnesium Alloys, John Demopoulos
Williams Honors College, Honors Research Projects
The purpose of this project was to increase the corrosion resistance of aluminum and magnesium alloys by coating the coupons with a silane on the surface. Four different silanes: 3-aminopropyltriethoxysilane (APTES), Bis(triethoxysilylpropyl)amine (Bis), (Heptadecafluoro-1,1,2,2-tetrahydrodecyl)trichlorosilane (FTS), and (Heptadecafluoro-1,1,2,2-tetrahydrodecyl)triethoxysilane (non Cl FTS) will be used and compared to see which silane would give the best corrosion resistance. Each silane solution was coated on the coupons by using a solution method in which the coupon was submerged for 24 hours and then thermally cured for another 24 hours. Once the coating was applied, the water contact angle and the thickness of the coating …
Passivation And Potential Fluctuation Of Az31b Alloy In Alkaline Environments, Ana C. Bacco
Passivation And Potential Fluctuation Of Az31b Alloy In Alkaline Environments, Ana C. Bacco
Williams Honors College, Honors Research Projects
Magnesium (Mg) alloys are used in many industries because of their distinctive properties, but their high chemical reactivity and poor oxide film protection make them inferior. This project focused on investigating the effects of secondary phases and intermetallic particles (IMPs) on the corrosion behavior of AZ31B Mg alloy. The test solution was chloride free NaOH with varying pH levels between 10-14, as well as testing under deaerated conditions. The open circuit potential (OCP) measurements using AZ31B in static NaOH solutions showed potential fluctuation between approximately -1.6 VSCE (active state) and -0.4 VSCE (passive state) during the 24-h immersion. …