The Effects Of Heat Treatment On Area Percent Porosity And Corrosion Behavior Of High-Nickel Thermal Spray Coatings, Travis Crowe, Alec Guraydin
The Effects Of Heat Treatment On Area Percent Porosity And Corrosion Behavior Of High-Nickel Thermal Spray Coatings, Travis Crowe, Alec Guraydin
Materials Engineering
Samples of two Thermal Spray Coating (TSC) alloys on a low carbon steel substrate were obtained: alloy C276 and Nicko-Shield 200. Specimens of each alloy were subjected to heat treatments at temperatures at 1100° for 60 minutes and 1200° for 10 minutes, with some specimens left in the as-sprayed condition. Three replicates were prepared for each condition. Thin 1” strips were cut using a diamond wafering blade for porosity measurements and 2” x 1” specimens were cut for corrosion testing using a SiC abrasive saw. The porosity specimens were mounted in acrylic resin, polished, and examined using SEM. From these …
Process Refinement Through Design Of Experiments (Taguchi) To Reduce Porosity Levels Of Thin Flame Spray Nicrbsi Coatings On Cast Aluminium Alloys, David Culliton, David Kennedy, Tony Betts
Process Refinement Through Design Of Experiments (Taguchi) To Reduce Porosity Levels Of Thin Flame Spray Nicrbsi Coatings On Cast Aluminium Alloys, David Culliton, David Kennedy, Tony Betts
Conference Papers
Thin(16matrix of key deposition parameters was constructed to develop the optimum spray parameters. The effects of parameter variations on the porosity levels of these coatings were assessed. Key parameter interactions were reported. Quantifiable interactions between the selected parameters were noted for the LM24 substrate. However, on the LM25 substrate these interactions were much less defined. Corrosion performance of the optimised coatings, based on electrochemical impedance spectroscopy, was reported. The presence of through-pores in the coatings were shown to reduce the corrosion resistance of the coated systems by a factor of 10, in dilute NaCl solutions, compared to bulk 316L stainless …