Full-Text Articles in Engineering
Rust-Expansion-Crack Service Life Prediction Of Existing Reinforced Concrete Bridge/Viaduct Using Time-Dependent Reliability Analysis, Ming-Te Liang, Jiang-Jhy Chang, Han-Tung Chang, Chi-Jang Yeh
Rust-Expansion-Crack Service Life Prediction Of Existing Reinforced Concrete Bridge/Viaduct Using Time-Dependent Reliability Analysis, Ming-Te Liang, Jiang-Jhy Chang, Han-Tung Chang, Chi-Jang Yeh
Journal of Marine Science and Technology
It is necessary to develop a calculation method to help in the making of feasible, reliable, and serviceable predictions for the service lives of bridge or viaduct structures. This article presents the basis for doing rust-expansion-crack service life predictions for existing reinforced concrete (RC) bridges and viaducts in chloride-laden environments based on timedependant reliability modeling due to the corrosion of steel in concrete. The corrosion process has three stages, the initiation (diffusion or carbonation) time (ti = tc), the depassivation time (tp), and the propagation (corrosion) time (tcorr). The rustexpansion-crack service lives (tcr) of existing RC bridges or viaducts can …
Degradation Of Automotive Materials In Palm Biodiesel
Degradation Of Automotive Materials In Palm Biodiesel
A.S. Md Abdul Haseeb
As compared to petroleum diesel, biodiesel is more corrosive for automotive materials. Studies on the characterization of corrosion products of fuel exposed automotive materials are scarce. Automotive fuel system and engine components are made from different ferrous and non-ferrous materials. The present study aims to investigate the corrosion products of different types of automotive materials such as copper, brass, aluminum and cast iron upon exposure to diesel and palm biodiesel. Changes in fuel properties due to exposure of different materials were also examined. Degradation of metal surface was characterized by digital camera, SEM/EDS and X-ray diffraction (XRD). Fuel properties were …