The Effect Of Flinak Molten Salt Corrosion On The Hardness Of Hastelloy N, David Kok
The Effect Of Flinak Molten Salt Corrosion On The Hardness Of Hastelloy N, David Kok
Scholar Week 2016 - present
The Molten Salt Reactor (MSR) has been identified as a promising candidate to replace aging nuclear reactors around the world. However, a suitable combination of molten salt and container material needs to be found in order to reduce the potential for corrosion in the MSR before it can be considered commercially viable. FLiNaK molten salt and the nickel-based alloy Hastelloy N have been identified as prime candidates for this function, but the severity of FLiNaK corrosion in Hastelloy N requires additional study before this combination can be used in the operation of a MSR. In this study, Hastelloy N samples …
An Electrochemical Analysis Of Fretting Corrosion In Metal-On-Metal Hip Implants Subjected To High Impaction Loads, Joe Morin, Timothy L. Norman, Thomas K. Fehring
An Electrochemical Analysis Of Fretting Corrosion In Metal-On-Metal Hip Implants Subjected To High Impaction Loads, Joe Morin, Timothy L. Norman, Thomas K. Fehring
The Research and Scholarship Symposium (2013-2019)
The metal-on-metal total hip arthroplasty, a procedure where the hip joint is replaced by a femoral prosthesis with a metal femoral head and a metal socket, has been a popular option for patients requiring a hip joint replacement. Metal on metal hip implants have been a successful implant design until recently where there has been an increased number of failures of this type of implant due to fretting corrosion, believed to be caused from the use of large femoral heads. Fretting corrosion in hip implants results from cyclic micromotion at the taper-trunnion interface; this interface motion removes the protective oxidation …