Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla
Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla
Publications
Reinforced Concrete (RC) structures are vital to the US’s civil infrastructure for their strength and versatility. Unfortunately, RC elements deteriorate rapidly when exposed to corrosive environments. One possible solution is to extend the life of RC elements and systems using microencapsulated corrosion inhibitors to reduce the rebar corrosion rate. The capsules house an anodic corrosion inhibitor agent including calcium nitrate (CN) and triethanolamine (TEA). The integration of such microencapsulated materials will enhance the durability and extend the useful life by controlling the corrosion precursors and the corrosion process during damage evolution. Therefore, this work aims to develop and characterize the …
Evaluation Of The Performance And Cost-Effectiveness Of Engineered Cementitious Composites (Ecc) Produced From Region 6 Local Materials, Gabriel Andres Arce Amador, Tyson Rupnow, Marwa Hassan
Evaluation Of The Performance And Cost-Effectiveness Of Engineered Cementitious Composites (Ecc) Produced From Region 6 Local Materials, Gabriel Andres Arce Amador, Tyson Rupnow, Marwa Hassan
Publications
The project objective is to develop cost-effective Engineered Cementitious Composites (ECC) with locally available ingredients in Region 6 to address the deficiencies observed in ordinary concrete materials. The study explored the utilization of two types of river sands (coarse and fine), two types of PVA fibers (long and short), four levels of cement replacement with Class F fly ash, and the implementation of recycled crumb rubber in the performance of ECC materials. A total of 24 mix designs were prepared and evaluated in compression, tension, and bending to assess its mechanical properties. Furthermore, the cracking characteristics of the materials produced …
Bridge Deck Overlays Using Ultra-High Performance Concrete, Craig Newtson, Brad Weldon
Bridge Deck Overlays Using Ultra-High Performance Concrete, Craig Newtson, Brad Weldon
Publications
This study investigated the use of a locally produced ultra-high performance concrete (UHPC) as an alternative to typical overlay materials. Several bond strength tests including slant-shear, splitting tension, and direct tension tests were performed to assess the bond strength between UHPC and normal strength concrete (NSC) substrate with varying surface textures. Tests were also conducted to assess the early-age and longer-term shrinkage behavior and coefficient of thermal expansion of the UHPC as well as rapid chloride permeability testing. Good bond between UHPC and NSC substrate was observed even with inadequate surface texture. Combined shrinkage and thermal effects were investigated for …