Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Carmine Vittoria
BaO(Fe₂O₃)₆ (BaM) thin films were deposited by pulsed laser deposition on GaN/Al₂O₃ substrates. A pole figure obtained from the (006) reflection indicated that ~81% of the film volume had the c axis tilted less than 5° from the film normal. A low anisotropy field was inferred from vector coil vibrating sample magnetometer (VVSM) measurements. The reduction in Hₐ from literature values and a two-step switching of the easy axis magnetization is postulated to result from interdiffusion and misalignment effects. To alleviate interdiffusion and to improve the c-axis alignment, experiments were repeated with lower deposition temperatures, thinner films, and MgO buffer …
Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Vincent G. Harris
BaO(Fe₂O₃)₆ (BaM) thin films were deposited by pulsed laser deposition on GaN/Al₂O₃ substrates. A pole figure obtained from the (006) reflection indicated that ~81% of the film volume had the c axis tilted less than 5° from the film normal. A low anisotropy field was inferred from vector coil vibrating sample magnetometer (VVSM) measurements. The reduction in Hₐ from literature values and a two-step switching of the easy axis magnetization is postulated to result from interdiffusion and misalignment effects. To alleviate interdiffusion and to improve the c-axis alignment, experiments were repeated with lower deposition temperatures, thinner films, and MgO buffer …
Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Magnetic Anisotropy And Crystalline Texture In Bao(Fe₂O₃)₆ Thin Films Deposited On Gan/Al₂O₃, Paul R. Ohodnicki, K. Y. Goh, Yuranan Hanlumyuang, K. Ramos, Michael E. Mchenry, Zhuhua Cai, Katherine Ziemer, Hadis Morkoc, Necmi Biyikli, Zhaohui Chen, C. Vittoria, Vincent Girard Harris (1962-)
Katherine S. Ziemer
BaO(Fe₂O₃)₆ (BaM) thin films were deposited by pulsed laser deposition on GaN/Al₂O₃ substrates. A pole figure obtained from the (006) reflection indicated that ~81% of the film volume had the c axis tilted less than 5° from the film normal. A low anisotropy field was inferred from vector coil vibrating sample magnetometer (VVSM) measurements. The reduction in Hₐ from literature values and a two-step switching of the easy axis magnetization is postulated to result from interdiffusion and misalignment effects. To alleviate interdiffusion and to improve the c-axis alignment, experiments were repeated with lower deposition temperatures, thinner films, and MgO buffer …
Influence Of Reactive Atmosphere On Properties Of Cobalt Ferrite Thin Films Prepared Using Pulsed-Laser Deposition, A. Raghunathan, David C. Jiles, J. E. Snyder
Influence Of Reactive Atmosphere On Properties Of Cobalt Ferrite Thin Films Prepared Using Pulsed-Laser Deposition, A. Raghunathan, David C. Jiles, J. E. Snyder
David C. Jiles
A series of cobaltferrite (CFO) thin films were grown on SiO2/Si(100) substrates using pulsed-laser deposition (PLD) at substrate temperature (T DEP) of 250 °C and oxygen pressures (P O2) from 0.67 to 6.7 Pa. The influence of PO2 on crystal structure, phase mixture, deposition rate, and magnetic properties was investigated. It is shown in this study that there is a window of PO2 for optimized growth of nanograined CFO films at low T DEP and that either higher or lower values of PO2 produce undesirable multiphase mixtures. CFO filmsgrown at such low substrate temperature and optimized oxygen pressure on thermal …