High-Quality P-N Junctions With Quaternary Alingan/Ingan Quantum Wells, A. Chitnis, A. Kumar, M. Shatalov, V. Adivarahan, A. Lunev, J. W. Yang, Grigory Simin, M. Asif Khan, R. Gaska, M. Shur
High-Quality P-N Junctions With Quaternary Alingan/Ingan Quantum Wells, A. Chitnis, A. Kumar, M. Shatalov, V. Adivarahan, A. Lunev, J. W. Yang, Grigory Simin, M. Asif Khan, R. Gaska, M. Shur
Faculty Publications
We report on quaternary AlInGaN/InGaN multiple quantum well(MQW)light emitting diode structures grown on sapphire substrates. The structures demonstrate high quality of the p–njunctions with quaternary MQW. At low forward bias (below 2 V), the temperature dependent of current–voltage characteristics are exponential with the ideality factor of 2.28, which is in a good agreement with the model of the injected carrier recombination in the space charge region. This ideality factor value is approximately three times lower than for conventional GaN/InGaN light emitting diodes(LEDs). The obtained data indicate the recombination in p–njunction space charge region to be responsible for a current transport …
Enhanced Luminescence In Ingan Multiple Quantum Wells With Quaternary Alingan Barriers, Jianping Zhang, J. Yang, Grigory Simin, M. Shatalov, M. Asif Khan, M. S. Shur, R. Gaska
Enhanced Luminescence In Ingan Multiple Quantum Wells With Quaternary Alingan Barriers, Jianping Zhang, J. Yang, Grigory Simin, M. Shatalov, M. Asif Khan, M. S. Shur, R. Gaska
Faculty Publications
We report on the comparative photoluminescence studies of AlGaN/GaN, GaN/InGaN, and AlInGaN/InGaN multiple quantum well(MQW) structures. The study clearly shows the improvement in materials quality with the introduction of indium. Our results point out the localized state emission mechanism for GaN/InGaN structures and the quantum well emission mechanism for AlInGaN/InGaN structures. The introduction of indium is the dominant factor responsible for the observed differences in the photoluminescence spectra of these MQW structures.
Selective Area Deposited Blue Gan-Ingan Multiple-Quantum Well Light Emitting Diodes Over Silicon Substrates, J. W. Yang, A. Lunev, Grigory Simin, A. Chitnis, M. Shatalov, M. Asif Khan, Joseph E. Van Nostrand, R. Gaska
Selective Area Deposited Blue Gan-Ingan Multiple-Quantum Well Light Emitting Diodes Over Silicon Substrates, J. W. Yang, A. Lunev, Grigory Simin, A. Chitnis, M. Shatalov, M. Asif Khan, Joseph E. Van Nostrand, R. Gaska
Faculty Publications
We report on fabrication and characterization of blue GaN–InGaN multi-quantum well (MQW)light-emitting diodes(LEDs) over (111) silicon substrates. Device epilayers were fabricated using unique combination of molecular beam epitaxy and low-pressure metalorganic chemical vapor depositiongrowth procedure in selective areas defined by openings in a SiO2mask over the substrates. This selective area deposition procedure in principle can produce multicolor devices using a very simple fabrication procedure. The LEDs had a peak emission wavelength of 465 nm with a full width at half maximum of 40 nm. We also present the spectral emission data with the diodes operating up to 250 …