Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla
Self-Healing Microcapsules As Concrete Aggregates For Corrosion Inhibition In Reinforced Concrete, Homero Castaneda, Marwa Hassan, Miladin Radovic, Jose Milla
Publications
Reinforced Concrete (RC) structures are vital to the US’s civil infrastructure for their strength and versatility. Unfortunately, RC elements deteriorate rapidly when exposed to corrosive environments. One possible solution is to extend the life of RC elements and systems using microencapsulated corrosion inhibitors to reduce the rebar corrosion rate. The capsules house an anodic corrosion inhibitor agent including calcium nitrate (CN) and triethanolamine (TEA). The integration of such microencapsulated materials will enhance the durability and extend the useful life by controlling the corrosion precursors and the corrosion process during damage evolution. Therefore, this work aims to develop and characterize the …
A Comparative Study On The Durability Of Geopolymer Mortars Produced With Ground Glass Fiber, Fly Ash, And Glass-Powder In Sodium Sulfate Solution, Hassan Rashidian-Dezfouli, Prasada Rao Rangaraju
A Comparative Study On The Durability Of Geopolymer Mortars Produced With Ground Glass Fiber, Fly Ash, And Glass-Powder In Sodium Sulfate Solution, Hassan Rashidian-Dezfouli, Prasada Rao Rangaraju
Publications
An experimental investigation was conducted to investigate the performance of geopolymers made with three different precursors consisting of fly ash, Ground Glass Fiber (GGF), and Glass-Powder (GLP) exposed to sodium sulfate solution. Precursors were activated using either sodium hydroxide solution or combinations of sodium hydroxide and sodium silicate solution with varying levels of sodium and silica content. Among the mixtures with each of the three precursors, mortar mixtures with the highest compressive strength were selected to test their resistance against exposure to a 5% sodium sulfate solution. Changes in the weight and compressive strength of the specimens were monitored up …