The Study Of Corrosion On Additive-Manufactured Metals., Braydan Daniels
The Study Of Corrosion On Additive-Manufactured Metals., Braydan Daniels
Electronic Theses and Dissertations
The purpose of this study was to investigate and compare the corrosion mechanisms between wrought and additive-manufactured (3D-printed) copper and stainless steel. The experimental procedure consisted of measuring the open circuit potential, electrochemical impedance spectroscopy, linear sweep voltammetry, Tafel analysis, surface topology, and scanning electron microscopy for each metal within salt water, tap water, sulfuric acid, and synthetic body fluid (excluding copper in synthetic body fluid).
Overall, printed stainless steel was more corrosion-resistant than wrought stainless steel in tap water and synthetic body fluid based on OCP, LSV, and surface topology results. Additionally, printed copper was more corrosion-resistant than wrought …
Multifunctional Corrosion Inhibition Behavior Of Zn-Al Calcined Layered Double Hydroxides For Steel Rebar In Nacl Solution, Xiao-Juan Zhang, Jing-Jing Wang, Shi-Gang Dong, Chang-Jian Lin
Multifunctional Corrosion Inhibition Behavior Of Zn-Al Calcined Layered Double Hydroxides For Steel Rebar In Nacl Solution, Xiao-Juan Zhang, Jing-Jing Wang, Shi-Gang Dong, Chang-Jian Lin
Journal of Electrochemistry
The Zn-Al layered double hydroxides (Zn-Al LDHs) and calcined products (Zn-Al CLDHs) were synthesized successfully under a routine air atmosphere. The results showed that both Zn-Al LDHs and Zn-Al CLDHs had obvious flake structures. The corrosion inhibition of Zn-Al CLDHs for steel rebar in NaCl solution was studied by electrochemical techniques. It was found that the corrosion rate of steel rebar decreased significantly after the steel rebar was treated by Zn-Al CLDHs in NaCl solution for 3 h. It was indicated that Zn-Al CLDHs could absorb Cl- and release OH- during their reconstruction process, which provided dual protection …
Avoid Sulfuric Acid Corrosion In Metallic Stacks, João F. Gomes
Avoid Sulfuric Acid Corrosion In Metallic Stacks, João F. Gomes
João F Gomes
Acidic gaseous effluents frequently cause corrosion on metallic stacks. This paper presents a method for prevision of probability of corrosion occurrence caused by gaseous effluents containing sulphur oxides which is based on the sulphur trioxide and moisture content measured in stack
Synthesis And Application Of Polymeric Corrosion Inhibitor For Reinforced Concrete, Weiwei Lin, Shengxian Wang, Jianqing Zhang
Synthesis And Application Of Polymeric Corrosion Inhibitor For Reinforced Concrete, Weiwei Lin, Shengxian Wang, Jianqing Zhang
Journal of Electrochemistry
A new polymer E Twas synthesized and used as a corrosion inhibitor for reinforced concrete. The inhibitive behavior and mechanism were studied with linear polarization ,Tafel polarization,EIS and XPS method in simulated pore solution system with concrete samples.The result showed that the polymer was a mixing type inhibitor. A 1% dosage was sufficient to imhibit the corrosion of steel in simulated pore solution system. The salt endurance was enhanced from 0.02 mol/L to 0.10 mol/L.The result also showed the good synergetic effect of NaNO 2,especially in low NaNO 2 concentration.The EIS showed that E_T has dual function on reinforced concrete,i.e.,densifying …