Open Access. Powered by Scholars. Published by Universities.®
Articles 1 - 3 of 3
Full-Text Articles in Engineering
Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner
Evaluation Of Corrosion Properties Of Proprietary Metal Alloy Stents For In-Vivo Use, Michael David Bremner
Materials Engineering
To assess corrosion rates of metal alloy bio-absorbable stents an experimental set-up was designed to mimic the coronary artery environment. The artery was modeled using 4mm diameter Tecoflex tubing and the metal alloy stents were inserted into the tubing using a catheter. As is the case in cardiac surgery, the catheter with the stent and a microballoon were maneuvered to the desired position. The microballoon was then slowly inflated to expand the stent and compress it against the tubing walls. The catheter and microballoon were then withdrawn. A circulating pump system was set up to cycle fetal bovine serum (FBS) …
Evaluation Of Corrosion Properties For Use Of Az31b In Bioabsorbable Stents And In Vivo Corrosion Rate Prediction Using Fea, Jared Vidales, Austin Schader, Jenna Jerman, Michael Turovskiy
Evaluation Of Corrosion Properties For Use Of Az31b In Bioabsorbable Stents And In Vivo Corrosion Rate Prediction Using Fea, Jared Vidales, Austin Schader, Jenna Jerman, Michael Turovskiy
Materials Engineering
AZ31B was heat treated to evoke more controlled and uniform corrosion. 1/16” diameter AZ31B wire was cut into six samples each 1” long. The samples underwent heat treatments following ASTM B661-06. Samples were weighed and placed into three different in vitro environments. In the first scenario two samples of each heat treatment were individually placed in 50 ml of saline solution at 0.9% sodium, in a static test tube at 37°C temperature. Two samples were placed in 100 ml of 0.9% saline solution in a 250 ml stirring beaker with an average whirlpool depth of 1”. Two of each sample …
Corrosion Of Stainless Steel 316l And Astm F75 Cobalt Chromium Alloy During Immersion Testing In Silver Salt Solutions, Meagan Higgins
Corrosion Of Stainless Steel 316l And Astm F75 Cobalt Chromium Alloy During Immersion Testing In Silver Salt Solutions, Meagan Higgins
Materials Engineering
This study evaluates the potential effects of silver salts on biocompatible metals used for prostheses during the chemical reduction process to produce a silver antimicrobial layer on the metal’s surface. Samples of two biocompatible metals were obtained: Stainless Steel 316L and ASTM F75 Cobalt Chromium Alloy. Three different silver salts were also acquired: silver nitrate, silver sulfadiazine, and silver chloride. Specimens of each metal were cut to size using a 4-1/2 inch aluminum oxide, 40 grit, cut off wheel for metal, attached to a Dewalt Angle Grinder. The biocompatible metal samples were then subject to either Solution 1, water with …