Enhancement Of The Refrigerant Capacity In Low Level Boron Doped La0.8gd0.2fe11.4si1.6, P Shamba, R Zeng, Jianli Wang, S J. Campbell, S X. Dou

Jianli Wang

The effects of boron doping on the itinerant-electron metamagnetic (IEM) transition and the magnetocaloric effects (MCEs) in the cubic NaZn13-type La0.8Gd0.2Fe11.4Si1.6 compound have been investigated. The Curie temperature, TC, of La0.8Gd0.2Fe11.4Si1.6Bx compounds with x=0, 0.03, 0.06, 0.2 and 0.3 was found to increase from 200 K to 222 K with increase in boron doping, x. The maximum values of the isothermal magnetic entropy change, ΔSM, (derived using the Maxwell relation for a field change ΔB=0-5 T) in La0.8Gd0.2Fe11.4Si1.6Bx with x=0, 0.03, 0.06, 0.2 and 0.3 are 14.8, 16, 15, 7.5 and 6.6 J kg−1 K−1 respectively, with corresponding values of …