Open Access. Powered by Scholars. Published by Universities.®
Physical Sciences and Mathematics Commons™
Open Access. Powered by Scholars. Published by Universities.®
Articles 1 - 3 of 3
Full-Text Articles in Physical Sciences and Mathematics
Reduction Of Benzylidene Dibenzo[ A, D ]Cycloheptenes: Over-Reduction Of Antiaromatic Dianions To Aromatic Tetraanions, Blakely Tresca, Macdonald Higbee, Nancy S. Mills
Reduction Of Benzylidene Dibenzo[ A, D ]Cycloheptenes: Over-Reduction Of Antiaromatic Dianions To Aromatic Tetraanions, Blakely Tresca, Macdonald Higbee, Nancy S. Mills
Chemistry Faculty Research
The antiaromaticity of a series of dianions of p-substituted benzylidene dibenzo[a,d]cycloheptenes was examined through calculated measures of antiaromaticity. The nucleus-independent chemical shifts (NICS) and magnetic susceptibility exaltation both showed substantial antiaromatic character in the benzannulated tropylium anion. When the antiaromaticity was normalized for the area of the ring, these tropylium anions were shown to be among the most antiaromatic anions in the chemical literature. Attempts to make the dianion through reduction with lithium or potassium gave the tetraanion as the only species observable in the (1)H NMR spectrum. Quench of the reaction mixture with trimethylsilyl chloride or D(2)O confirmed the …
Enhanced Oxygen Activation Over Supported Bimetallic Au-Ni Catalysts, Bert D. Chandler, Cormac G. Long, John D. Gilbertson, Christopher J. Pursell, G. Vijayaraghavan, K. J. Stevenson
Enhanced Oxygen Activation Over Supported Bimetallic Au-Ni Catalysts, Bert D. Chandler, Cormac G. Long, John D. Gilbertson, Christopher J. Pursell, G. Vijayaraghavan, K. J. Stevenson
Chemistry Faculty Research
New bimetallic Ni-Au supported nanoparticle catalysts were prepared by using dendrimer templated nanoparticles. Amine-terminated generation 5 polyamidoamine (PAMAM) dendrimers were anchored to a commercial silica with a siloxane linked anhydride. The dendrimer was then alkylated and used to template Ni-Au nanoparticles, which were subsequently extracted into organic solution as thiol monolayer protected clusters (MPCs). Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) indicated bimetallic nanoparticles of about 2 nm in size. Nanoparticles were deposited onto P-25 TiO2, and the capping thiol ligands were removed under flowing H2. DRIFTS infrared spectra of adsorbed CO showed only Au on the catalyst …
Preparation And Characterization Of 3 Nm Magnetic Niau Nanoparticles, Bethany J. Auten, B. P. Hahn, G. Vijayaraghavan, K. J. Stevenson, Bert D. Chandler
Preparation And Characterization Of 3 Nm Magnetic Niau Nanoparticles, Bethany J. Auten, B. P. Hahn, G. Vijayaraghavan, K. J. Stevenson, Bert D. Chandler
Chemistry Faculty Research
Using PAMAM dendrimers as nanoparticle templates, a synthetic route to prepare 3 nm magnetic NiAu nanoparticles was developed. Aqueous solutions of hydroxyl-terminated generation 5 PAMAM dendrimers in 25 mM NaClO4 were shown to bind aqueous NiII. Coreduction of NiII and AuIII salts yielded bimetallic dendrimer stabilized nanoparticles, which were extracted into toluene with decanethiol. Characterization of the resulting monolayer protected clusters (MPCs) with transmission electron microscopy and UV–visible, atomic absorption, and X-ray photoelectron spectroscopies suggested that the MPCs had substantial surface enrichment in Au. Superconducting quantum interference device (SQUID) measurements at 5 K show the …