Thin Film Carbon Nanofuses For Permanent Data Storage, Kevin Robert Laughlin
Thin Film Carbon Nanofuses For Permanent Data Storage, Kevin Robert Laughlin
Theses and Dissertations
We have fabricated nanofuses from thin-film, arc-evaporation carbon for use in permanent data storage. Thin film carbon fuses have fewer fabrication barriers and retain the required resistivity and structural stability to work as a data storage medium. Carbon thin films were characterized for their electrical, microstructural, and chemical bonding properties. Annealing the thin-film carbon in an argon environment at 400°C reduced the resistivity from about 4*10-2 Ω cm as deposited down to about 5*10-4 Ω cm, allowing a lower blowing voltage. Nanofuses with widths ranging from 200 nm down to 60 nm were fabricated and tested. They blow …
Β-Delayed Proton Decay Of 9c, David D. Allred, John E. Esterl, J. C. Hardy, R. G. Sextro, Joseph Cerny
Β-Delayed Proton Decay Of 9c, David D. Allred, John E. Esterl, J. C. Hardy, R. G. Sextro, Joseph Cerny
Faculty Publications
The delayed-proton spectrum following the β decay of 9C (t1/2=126.5±1.0 msec) was found to consist primarily of a continuum extending from 13 to 1.5 MeV, the latter being the lowest energy observed. In addition to the previously observed peaks at 9.28 and 12.30 MeV (C.M.), possible peaks between 3 and 7 MeV have been tentatively identified.