Microstructures And Hardness Of Tig Welded Experimental 57fe15cr25ni Steel, Parikin Parikin, Mohammad Dani, Abu Khalid Rivai, Agus Hadi Ismoyo, Riza Iskandar, Arbi Dimyati
Microstructures And Hardness Of Tig Welded Experimental 57fe15cr25ni Steel, Parikin Parikin, Mohammad Dani, Abu Khalid Rivai, Agus Hadi Ismoyo, Riza Iskandar, Arbi Dimyati
Makara Journal of Technology
The microstructures and hardness of tungsten inert gas (TIG) welded experimental 57Fe15Cr25Ni steel were investigated through optical–scanning electron microscopy analyses and with a hardness tester, respectively. The welding process restructured the constituent atoms into regular and irregular crystal lattices. Rapid cooling of the weld metal allowed the formation of a dendritic (columnar) structure, with porous grains. By contrast, slow cooling influenced HAZ and led to the formation of grain structures. The crystal lattice became more organized and larger than other zones. Meanwhile, the base metal formed circular nets that covered large area inside thick and thin grain boundaries. The diffraction …
Influence Of Natural Convection During Dendritic Array Growth Of Metal Alloys (Gradient Freeze Directional Solidification), Suyog N. Mahajan
Influence Of Natural Convection During Dendritic Array Growth Of Metal Alloys (Gradient Freeze Directional Solidification), Suyog N. Mahajan
ETD Archive
Purpose of this study was to examine the microstructural evolution of primary dendrites during Gradient Freeze Directional Solidification process in cylindrical Pb-5.8% Sb alloy samples to generate the ground- based research data to support a future microgravity experiment on the Space Station in a convection free environment. Pb-5.8Sb was selected for this study because of its ease of processing and availability of physical property data which will be required for predicting the dendrite morphology parameters, such as, primary dendrite spacing and dendrite trunk diameter. This alloy is also susceptible to thermosolutal convection caused by density inversion of the met in …