Spark Plasma Sintering Of Magnesium Titanate Ceramics, Suzana Filipović, Nina Obradović, William G. Fahrenholtz, Steven Smith, Miljana Mirković, Adriana Peleš Tadić, Jovana Petrović, Antonije Đorđević
Spark Plasma Sintering Of Magnesium Titanate Ceramics, Suzana Filipović, Nina Obradović, William G. Fahrenholtz, Steven Smith, Miljana Mirković, Adriana Peleš Tadić, Jovana Petrović, Antonije Đorđević
Materials Science and Engineering Faculty Research & Creative Works
Magnesium titanate ceramics were prepared by reactive spark plasma sintering (SPS) at 1200 °C for 5 min. Prior to sintering, MgO and TiO2 powders were mixed by high energy ball milling (HEBM) for 15, 30, or 60 min. The effect of milling time on phase composition was analyzed by X-ray diffraction (XRD) for milled powders and sintered specimens. The morphology of the sintered ceramics was investigated by scanning electron microscopy (SEM), while elemental distribution was determined by energy dispersive spectroscopy (EDS). The presence of the MgTi2O5 phase was detected in XRD and was confirmed by EDS analysis. Microcracking was …
A Super-Hard High Entropy Boride Containing Hf, Mo, Ti, V, And W, Suzana Filipovic, Nina Obradovic, Greg E. Hilmas, William G. Fahrenholtz, Donald W. Brenner, Jon Paul Maria, Douglas E. Wolfe, Eva Zurek, Xiomara Campilongo, Stefano Curtarolo
A Super-Hard High Entropy Boride Containing Hf, Mo, Ti, V, And W, Suzana Filipovic, Nina Obradovic, Greg E. Hilmas, William G. Fahrenholtz, Donald W. Brenner, Jon Paul Maria, Douglas E. Wolfe, Eva Zurek, Xiomara Campilongo, Stefano Curtarolo
Materials Science and Engineering Faculty Research & Creative Works
Super-Hard (Hf,Mo,Ti,V,W)B2 Was Synthesized by Boro-Carbothermal Reduction and Densified by Spark Plasma Sintering. This Composition Was Produced for the First Time as a Single-Phase Ceramic in the Present Research. the Optimized Ceramic Had a Single Hexagonal AlB2-Type Crystalline Phase with a Grain Size of 3.8 µm and Homogeneous Distribution of the Constituent Metals. the Vickers Hardness Exhibited the Indentation Size Effect, Increasing from 27 GPa at a Load of 9.8 N to as High as 66 GPa at a Load of 0.49 N. This is the Highest Hardness Reported to Date for High Entropy Boride Ceramics.