Articles 1 - 4 of 4
Full-Text Articles in Engineering
Mechanical Properties, Translucency, And Low Temperature Degradation (Ltd) Of Yttria (3–6 Mol%) Stabilized Zirconia, R. Sharon Uwanyuze, Sulekha Ramesh, Mark K. King, Nathaniel Lawson, Manoj K. Mahapatra
Mechanical Properties, Translucency, And Low Temperature Degradation (Ltd) Of Yttria (3–6 Mol%) Stabilized Zirconia, R. Sharon Uwanyuze, Sulekha Ramesh, Mark K. King, Nathaniel Lawson, Manoj K. Mahapatra
Materials Science and Engineering Faculty Research & Creative Works
The mechanical properties (hardness and biaxial flexural strength), optical properties (translucency and gloss), and low temperature degradation (LTD) of 3–6 mol% yttria stabilized zirconia have been investigated. The specimens were prepared by conventional solid-state sintering at 1400 °C. The mechanical and optical properties were evaluated for sintered and polished specimens. X-ray diffractometer (XRD) and scanning electron microscope (SEM) were used, respectively, for structural and microstructural investigation. LTD was determined by XRD analysis of the samples aged in a hydrothermal autoclave at 134 °C for 5–108 h. The mechanical and optical properties are found to be microstructure sensitive. The LTD, due …
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Scientific-technical journal
The use of non-standard modes of heat treatment increases the density of dislocations in the crystal structure of the α-phase and increases the wear resistance of carbon, low-alloy steels under various friction conditions, which is comparable to the results when heated to a standard temperature (Ac3+30÷50 °C). The preliminary extreme heating temperature is determined. After re-quenching at standard temperature and low tempering, the wear resistance of steels under various types of friction increases by up to 40 % compared to standard quenching.
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Scientific-technical journal
The use of non-standard modes of heat treatment increases the density of dislocations in the crystal structure of the α-phase and increases the wear resistance of carbon, low-alloy steels under various friction conditions, which is comparable to the results when heated to a standard temperature (Ac3+30÷50 °C). The preliminary extreme heating temperature is determined. After re-quenching at standard temperature and low tempering, the wear resistance of steels under various types of friction increases by up to 40 % compared to standard quenching.
Direct Energy Deposition Of Mo Powder Prepared By Electrode Induction Melting Gas Atomization, Goo Won Roh, Eun Soo Park, Jaeyun Moon, Hojun Lee, Jongmin Byun
Direct Energy Deposition Of Mo Powder Prepared By Electrode Induction Melting Gas Atomization, Goo Won Roh, Eun Soo Park, Jaeyun Moon, Hojun Lee, Jongmin Byun
Mechanical Engineering Faculty Research
Molybdenum (Mo) is used to form a barrier layer for metal wiring in displays or semiconductor devices. Recently, researches have been continuously attempted to fabricate Mo sputtering targets through additive manufacturing. in this study, spherical Mo powders with an average particle size of about 37 um were manufactured by electrode induction melting gas atomization. Subsequently, Mo layer with a thickness of 0.25 mm was formed by direct energy deposition in which the scan speed was set as a variable. According to the change of the scan speed, pores or cracks were found in the Mo deposition layer. Mo layer deposited …