Engineering Commons^™

Indentation Behavior Of Superelastic Hard Carbon, Olga Chernogorova, Ekaterina Drozdova, Iraida Ushakova, Evgenii Ekimov, Vicente Benavides, Aleksander Soldatov

Nanomechanical Testing in Materials Research and Development V

Supererlastic hard carbon particles up to 1 mmin size were produced by fullerene collapse upon high-pressure high-temperature treatment with simultaneous sintering of metal-matrix composite materials (CM) reinforced by such particles. The hardness of carbon particles can be varied in a wide range by changing the parameters of their structure, which consists of curved graphene planes or their packets of different sizes. Such carbon phase was called “nanoclusterd graphene phase” (NGP) [1]. The properties of the carbon particles were controlled by changing treatment pressure (5 and 8 GPa) and temperature (1100-1800 K), composition of parent fullerites (C60 or C60/70), and pre-treatment …