Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Scientific-technical journal
The use of non-standard modes of heat treatment increases the density of dislocations in the crystal structure of the α-phase and increases the wear resistance of carbon, low-alloy steels under various friction conditions, which is comparable to the results when heated to a standard temperature (Ac3+30÷50 °C). The preliminary extreme heating temperature is determined. After re-quenching at standard temperature and low tempering, the wear resistance of steels under various types of friction increases by up to 40 % compared to standard quenching.
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Influence Of Parameters Of Non-Standard Modes Of Heat Treatment On Increasing The Wear Resistance Of Steel Products, Dorob Murotovich Berdiyev Dsn, Abdulaziz Abdullajanovich Yusupov Head Teacher, Ravshan Kobilovich Tashmatov Doctoral Student, Tuychi Nemat Ogli Ibodullayev Assistant, Kabira Erkinovna Qurbonova Head Teacher
Scientific-technical journal
The use of non-standard modes of heat treatment increases the density of dislocations in the crystal structure of the α-phase and increases the wear resistance of carbon, low-alloy steels under various friction conditions, which is comparable to the results when heated to a standard temperature (Ac3+30÷50 °C). The preliminary extreme heating temperature is determined. After re-quenching at standard temperature and low tempering, the wear resistance of steels under various types of friction increases by up to 40 % compared to standard quenching.