Single Cuo Nanowires Electrical Properties And Application On Photoelectrochemical Water Splitting, Junnan Wu

McKelvey School of Engineering Theses & Dissertations

Charge transport in single crystal, p type copper oxide (CuO) nanowires (NWs) was studied through temperature based (120 K – 400 K) current-voltage (I-V) measurements of 2-terminal single NW devices. Individual CuO NWs with an average diameter of 220 nm were attached to Au electrodes 2.5 µm apart, using a dielectrophoresis method. I-V curves showed a transition from linear behavior at low bias to strong power law dependence (I ~ V^a) at high bias, which can be attributed to space charge limited current (SCLC) mechanism. At low electrical fields (< 0.89 × 10³ V·cm^-1), the number of …