Open Access. Powered by Scholars. Published by Universities.®

Engineering Commons

Open Access. Powered by Scholars. Published by Universities.®

2019

ECU Publications Post 2013

Iron alloys

Articles 1 - 2 of 2

Full-Text Articles in Engineering

Phase Separation And Enhanced Wear Resistance Of Cu88fe12 Immiscible Coating Prepared By Laser Cladding, Shuzhen Zhao, Shengfeng Zhou, Min Xie, Xiaoqin Dai, Dongchu Chen, Laichang Zhang Jan 2019

Phase Separation And Enhanced Wear Resistance Of Cu88fe12 Immiscible Coating Prepared By Laser Cladding, Shuzhen Zhao, Shengfeng Zhou, Min Xie, Xiaoqin Dai, Dongchu Chen, Laichang Zhang

ECU Publications Post 2013

In order to eliminate the microstructure segregation of Cu–Fe immiscible alloys which characterized with a liquid miscible gap, the Cu88Fe12 (wt.%) immiscible coating was prepared by laser cladding. The phase separation characteristic and wear resistance of the Cu88Fe12 (wt.%) immiscible coating were also investigated. The results show that the size of the milled Cu88Fe12 composite powder is reduced comparing to that of the un-milled powder due to fracturing during mechanical milling. Moreover, the demixing or delamination disappears in the Cu88Fe12 immiscible coating and a large amount of face-centered-cubic (fcc) γ-Fe and body-centered-cubic (bcc) α-Fe particles are dispersed in the ...


Deformation And Strength Characteristics Of Laves Phases In Titanium Alloys, Chirag D. Rabadia, Y. J. Liu, Liang-Yu Chen, Syed F. Jawed, L. Q. Wang, Hongqi Sun, Laichang Zhang Jan 2019

Deformation And Strength Characteristics Of Laves Phases In Titanium Alloys, Chirag D. Rabadia, Y. J. Liu, Liang-Yu Chen, Syed F. Jawed, L. Q. Wang, Hongqi Sun, Laichang Zhang

ECU Publications Post 2013

The superior reinforcement nature of Laves phases make them suitable for high-strength applications. Therefore, investigations on the deformation and strength characteristics of Laves phases are useful in development of an improved Laves phase-reinforced alloy. In this work, the Vickers micro-indentation method is used to evaluate and compare the deformation and strength characteristics of a hexagonal close-packed Laves phase (C14-type) in Ti-35Zr-5Fe-6Mn (wt%) and a face-centered cubic Laves phase (C15-type) in Ti-33Zr-7Fe-4Cr (wt%), considering the same volume fraction of Laves phase (~7.0%) in these alloys. Moreover, the effects of higher volume fraction of Laves phase (19.4%) on indentation-based deformation ...