Full-Text Articles in Engineering
(Bi0.51 Na0.47)Tio3 Based Lead Free Ceramics With High Energy Density And Efficiency, Yu Huang, Fei Li, Hua Hao, Fangquan Xia, Hanxing Liu, Shujun Zhang
(Bi0.51 Na0.47)Tio3 Based Lead Free Ceramics With High Energy Density And Efficiency, Yu Huang, Fei Li, Hua Hao, Fangquan Xia, Hanxing Liu, Shujun Zhang
Australian Institute for Innovative Materials - Papers
Dielectric ceramics with high energy storage density and energy efficiency play an important role in high power energy storage applications. In this work, lead free relaxor ferroelectric ceramics in (1-x)Bi 0.51 Na 0.47 TiO 3 - xBa(Zr 0.3 Ti 0.7 )O 3 (BNT-BZT100x: x = 0.20, 0.30, 0.40 and 0.50) system are fabricated by conventional solid-state sintering method. The BNT-BZT100x ceramics are sintered dense with minimal pores, exhibiting pseudocubic symmetry and strong relaxor characteristic. A high energy storage density of 3.1 J/cm 3 and high energy efficiency of 91% are simultaneously achieved in BNT-BZT40 ceramic with 0.1 mm in thickness, …
Dielectric And Piezoelectric Properties Of Textured Lead-Free Na0.5bi0.5tio3-Based Ceramics, Nannan Dong, Xiaoyi Gao, Fangquan Xia, Hanxing Liu, Hua Hao, Shujun Zhang
Dielectric And Piezoelectric Properties Of Textured Lead-Free Na0.5bi0.5tio3-Based Ceramics, Nannan Dong, Xiaoyi Gao, Fangquan Xia, Hanxing Liu, Hua Hao, Shujun Zhang
Australian Institute for Innovative Materials - Papers
This work provides a comparative study of the dielectric and piezoelectric properties of randomly oriented and textured 0.88Na 0.5 Bi 0.5 TiO 3 -0.08K 0.5 Bi 0.5 TiO 3 -0.04BaTiO 3 (88NBT) ceramics. Textured ceramics were fabricated by template grain growth (TGG) method using NaNbO 3 (NN) for templates. For textured ceramics with 4 wt% NN templates, a Lotgering factor of 96% and piezoelectric coefficient d 33 of 185 pC/N were obtained. Compared to the randomly oriented ceramics, textured ceramics show lower strain hysteresis (H = 7.6%), higher unipolar strain of 0.041% with corresponding large signal piezoelectric coefficient d 33* …