Aqueous Solution-Evaporation Route Synthesis And Phase Structural Research Of The Li-Rich Cathode Li1.23Ni0.09Co0.12Mn0.56O2 By In-Situ Xrd, Chong-Heng Shen, Shou-Yu Shen, Zhou Lin, Xiao-Mei Zheng, Hang Su, Ling Huang, Jun-Tao Li, Shi-Gang Sun
Aqueous Solution-Evaporation Route Synthesis And Phase Structural Research Of The Li-Rich Cathode Li1.23Ni0.09Co0.12Mn0.56O2 By In-Situ Xrd, Chong-Heng Shen, Shou-Yu Shen, Zhou Lin, Xiao-Mei Zheng, Hang Su, Ling Huang, Jun-Tao Li, Shi-Gang Sun
Journal of Electrochemistry
The Li-rich Li1.23Ni0.09Co0.12Mn0.56O2 material was synthesized via aqueous solution-evaporation route. The structure and morphology of the material were characterized by means of XRD and SEM. The results indicated that the single particle of the product was polygonal with the size of 330 nm and the structure was layered solid solution with a certain amount of Li2MnO3. Electrochemical tests showed that the first discharge capacity of the Li-rich layered material was 250.8 mAh·g-1 at 0.1C，the capacity retention was 86.5% after 40 cycles. Through in-situ XRD study a …
Synthesis And Electrochemical Properties Of Li(Ni0.5Co0.2Mn0.3)1-2xTiXNbXO2, Yong Tang, Qin-Lin Liao, Xiang-An Guo
Synthesis And Electrochemical Properties Of Li(Ni0.5Co0.2Mn0.3)1-2xTiXNbXO2, Yong Tang, Qin-Lin Liao, Xiang-An Guo
Journal of Electrochemistry
The cathode-active materials of layered Li(Ni0.5Co0.2Mn0.3)1-2xTixNbxO2（x=0, 0.002, 0.005, 0.01, 0.02）composites were synthesized by the thermal treatment of the coprecipitated precursor at 900 oC in air. The effects of Ti-Nb co-dopants on the structural and electrochemical properties of Li(Ni0.5Co0.2Mn0.3)O2 were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical experiments. The results show that the small amounts of Ti-Nb co-dopants in Li(Ni0.5Co0.2Mn0.3)O2significantly decreased the degree of cation mixing in …
Electrochemical Performance Of Al-Doped Spinel Limn2O4 Cathode Material For Li-Ion Batteries, Yong-Long Wang, Wen-Ge Wang, Qian Zhang, Xin Wang, Jian-Sheng Cao, Shi-Hai Ye
Electrochemical Performance Of Al-Doped Spinel Limn2O4 Cathode Material For Li-Ion Batteries, Yong-Long Wang, Wen-Ge Wang, Qian Zhang, Xin Wang, Jian-Sheng Cao, Shi-Hai Ye
Journal of Electrochemistry
Spinel LiMn2O4, a cathode material for Li-ion batteries, is featured as good high-rate performance, low cost and environmental friendly. The pristine and Al-doped LiMn2O4 samples were prepared by sol-gel method. The structure and micromorphology of the as-prepared samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results demonstrated that the as-prepared LiMn2O4 samples had a typical cubic spinel structure and were composed of sphere-like particles with a diameter range of 300 ~ 500 nm. Galvanostatic charge-discharge tests showed that the LiMn2O4 samples doped …