Electroluminescence Studies On Longwavelength Indium Arsenide Quantum Dot Microcavities Grown On Gallium Arsenide, John C. Ramsey
Electroluminescence Studies On Longwavelength Indium Arsenide Quantum Dot Microcavities Grown On Gallium Arsenide, John C. Ramsey
Theses and Dissertations
A comprehensive study of the electroluminescence of four GaAs/AlGaAs microcavity devices with InAs/GaInAs quantum dot active regions emitting near 1.3 µm was conducted. The four molecular beam epitaxial grown samples with AlAs oxide aperture confinement layers were fabricated, characterized, and optically modeled. Optical power transmission of the samples was modeled using Matlab and compared with measured transmission data. Resonant cavity light emitting diodes (RCLEDs) and three vertical cavity surface emitting laser (VCSEL) samples were fabricated and electro-optically characterized over a range of injection currents and temperatures. Devices achieved continuous wave room temperature lasing at 1.28 µm with an output power …
Synthesis And Characterization Of Cdse-Zns Core-Shell Quantum Dots For Increased Quantum Yield, Joshua James Angell
Synthesis And Characterization Of Cdse-Zns Core-Shell Quantum Dots For Increased Quantum Yield, Joshua James Angell
Master's Theses
Quantum dots are semiconductor nanocrystals that have tunable emission through changes in their size. Producing bright, efficient quantum dots with stable fluorescence is important for using them in applications in lighting, photovoltaics, and biological imaging. This study aimed to optimize the process for coating CdSe quantum dots (which are colloidally suspended in octadecene) with a ZnS shell through the pyrolysis of organometallic precursors to increase their fluorescence and stability. This process was optimized by determining the ZnS shell thickness between 0.53 and 5.47 monolayers and the Zn:S ratio in the precursor solution between 0.23:1 and 1.6:1 that maximized the relative …