Fiber Volume Fraction Effects On Fatigue Response Of A Scs-6/Ti-15-3 Metal Matrix Composite At Elevated Temperature, Sean C. Coghlan
Fiber Volume Fraction Effects On Fatigue Response Of A Scs-6/Ti-15-3 Metal Matrix Composite At Elevated Temperature, Sean C. Coghlan
Theses and Dissertations
The purpose of this study was to determine the effects of fiber volume fraction on the fatigue behavior of Silicon Carbide fiber-reinforced Titanium alloy, SCS-6/Ti-15-3. Three fiber volume fractions were investigated; 15%, 25%, and 42%. The tests were performed under fully-reversed, strain-controlled conditions at 427 °C. The primary objectives of this study were to develop a fatigue life diagram and to document the damage and failure mechanisms. Compressive loads on the slender specimens were kept from buckling the specimens through the use of a buckling guide. This device allows unrestricted axial movement of the composite, while preventing any out-of-plane motion. …
Residual Strength After Fatigue Of A Cross-Ply Metal Matrix Composite At Elevated Temperature, Alvin N. Ruiz
Residual Strength After Fatigue Of A Cross-Ply Metal Matrix Composite At Elevated Temperature, Alvin N. Ruiz
Theses and Dissertations
The objective of this study was to investigate the residual strength of a cross-ply, SCS-6/Ti-15-3, metal matrix composite (MMC) at elevated temperature (427 °C) when exposed to fatigue loading. Several specimens were subjected to a strain-controlled, fully reversed loading (R=-1), at various strain levels. The specimens were fatigued up to a portion of their life expectancy and then loaded to failure. Stress and strain data obtained during the test provided useful information for the macro-mechanical behavior of the material. It was determined that the residual strength was directly related to the amount of damage present in the matrix, meanwhile, the …