Fatigue Behavior Of An Advanced Sic/Sic Composite At Elevated Temperature In Air And In Steam, Devon T. Christensen
Fatigue Behavior Of An Advanced Sic/Sic Composite At Elevated Temperature In Air And In Steam, Devon T. Christensen
Theses and Dissertations
The fatigue behavior of an advanced Silicon Carbide/Silicon Carbide (SiC/SiC) ceramic matrix composite (CMC) was investigated at 1200 ˚C in laboratory air and in steam environments. The composite consisted of a SiC matrix reinforced with Boron Nitride (BN) coated Hi-Nicalon fibers woven into eight-harness-satin (8HS) weave plies. Tensile stress-strain behavior and tensile properties were also evaluated at 1200 ˚C. Tension-tension fatigue tests were conducted in both laboratory air and in steam at 1200 ˚C at frequencies of 0.1 Hz, 1.0 Hz, and 10 Hz. The tension-tension fatigue tests had a ratio of minimum stress to maximum stress of R = …
Effects Of Delamination On Composite Sandwich Structures Under Static And Fatigue Loading, Eugene Everett Eswonia
Effects Of Delamination On Composite Sandwich Structures Under Static And Fatigue Loading, Eugene Everett Eswonia
Master's Theses
This thesis will present the experimental and numerical analysis of composite sandwich structures under monotonic and fatigue loading. The sandwich skins were made of fiberglass and the core used was a closed cell PVC foam. Initial delaminations were introduced into the sandwich structures during manufacturing to see the effect of delamination size on the ultimate strength and monotonic fracture. Fiberglass rods, called shear keys, added to the foam core to determine whether or not they increased the strength of the test specimens. Furthermore, shear key locations were also varied and their effects noted. The fixed rate static behavior for all …