The Effect Of Cryogenic Treatment On The Fatigue Life Of Chrome Silicon Steel Compression Springs, Debra Lynn Smith

Dissertations (1934 -)

The purpose of this dissertation is to explore the effect of cryogenic treatment on the fatigue life of compression springs. Product manufacturers are constantly searching for ways to make their products last longer. This dissertation addresses three questions: (1) What is the effect of cryogenic treatment on the fatigue life of chrome silicon steel compression springs? Does the life increase, decrease, or remain the same? (2) What is the effect of cryogenic treatment on the Percent Load Loss (Stress Relaxation) of chrome silicon steel compression springs? (3) What are the possible changes in the material that cause these effects?

The …

Fatigue Testing And Computational Analysis Of A Spinal Implant, Timothy Helton

Electronic Theses and Dissertations

The following study investigates the fatigue behavior of a spinal implant developed by Synthes, Inc. to provide stability and off load pressure from the discs in the lumbar region. The installation process for the StenoFix design utilizes plastic deformations to customize the device to each individual patient, but also has potential to degrade fatigue behavior. Physical testing of two titanium alloys, Ti-6Al-7Nb and Ti-15Mo, was conducted on hydraulic test frames and compared to computational simulations which were carried out for the following scenarios: cyclic excitation following plastic deformation; variation of material property definition; variation of loading location; and three modifications …

Thermodynamic Approach To Fatigue Failure Analysis In Metals And Composite Materials, Mehdi Naderi Abadi

LSU Doctoral Dissertations

Fatigue is a dissipative process and must obey the laws of thermodynamics. In general, it can be hypothesized that the degradation of machinery components is a consequence of irreversible thermodynamic processes that disorder a component, and that degradation is a time dependent phenomenon with increasing disorder. This suggests that entropy —a fundamental parameter in thermodynamics that characterizes disorder— offers a natural measure of component degradation. The majority of the existing methods for prediction of fatigue are limited to the study of a single fatigue mode, i.e., bending or torsion or tension-compression. Further, the variability in the duty cycle in a …